HAIPLEN H90 T4 Taro Plast Polypropylene Homopolymer (Talc Filler, 20%)

General

Material Status

Availability

Filler / Reinforcement

Additive

Features

Appearance

Forms

Processing Method

Physical	Nominal Value	Unit	Test Method
Specific Gravity
--			ASTM D792
--		g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)		g/10 min	ASTM D1238, ISO 1133
Molding Shrinkage			ASTM D955
Flow		in/in
Across Flow		in/in
Water Absorption (73°F, 24 hr)		%	ASTM D570, ISO 62
Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Yield)		psi	ASTM D638, ISO 527-2
Tensile Elongation (Break)		%	ASTM D638, ISO 527-2
Flexural Strength
--		psi	ISO 178
Break		psi	ASTM D790
Impact	Nominal Value	Unit	Test Method
Notched Izod Impact		ft·lb/in	ASTM D256
Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (264 psi, Unannealed)		°F	ASTM D648, ISO 75-2/A
Vicat Softening Temperature
--		°F	ASTM D1525², ISO 306/A50²
--		°F	ASTM D1525³, ISO 306/B50³
CLTE - Flow		in/in/°F	ASTM D696
Flammability	Nominal Value	Unit	Test Method
Flame Rating - UL (0.0630 in)			UL 94
Additional Information
Notched Izod Impact Strength , ISO 180, 23°C: 30 J/m
Related Terminology
Product names can be difficult to match. You may have searched any one of these terms to find this product: HAIPLEN H90 T4, HAIPLEN , HAIPLENH90T4, H 90 T 4, H90 T4, H90, 90T, T4, H90T4, Polypropylene Homopolymer, PP Homopolymer, Polypropylene, PP, Taro Plast, PolypropyleneHomopolymer, PPHomopolymer, 90H
Features
Features may also be described by the following terms: Heat Stabilized, Heat-ageing Stabilized, Heat Ageing Stabilized, Heat-aging Stabilized, Heat Aging Stabilized, Low Viscosity.

Notes

¹Typical properties: these are not to be construed as specifications.

²Rate A (50°C/h), Loading 1 (10 N)

³Rate A (50°C/h), Loading 2 (50 N)

HAIPLEN H90 T4