Specific Gravity
|
|
|
|
|
--
|
|
|
ASTM D792 |
|
--
|
|
g/cm³
|
ISO 1183 |
|
Molding Shrinkage
|
|
|
ASTM D955 |
|
Flow
|
|
in/in
|
|
|
Across Flow
|
|
in/in
|
|
|
Water Absorption (73°F, 24 hr)
|
|
%
|
ASTM D570, ISO 62 |
|
Tensile Modulus
|
|
psi
|
ASTM D638, ISO 527-2 |
|
Tensile Strength (Break)
|
|
psi
|
ASTM D638, ISO 527-2 |
|
Tensile Elongation (Break)
|
|
%
|
ASTM D638, ISO 527-2 |
|
Flexural Modulus
|
|
psi
|
ASTM D790, ISO 178 |
|
Flexural Strength
|
|
|
|
|
--
|
|
psi
|
ISO 178 |
|
Break
|
|
psi
|
ASTM D790 |
|
Charpy Notched Impact Strength 2 (73°F)
|
|
ft·lb/in²
|
ASTM D256, ISO 179 |
|
Charpy Unnotched Impact Strength 2 (73°F)
|
|
ft·lb/in²
|
ASTM D256, ISO 179 |
|
Notched Izod Impact
|
|
|
|
|
-4°F, 0.126 in
|
|
ft·lb/in
|
ISO 180, ASTM D256 |
|
73°F, 0.126 in
|
|
ft·lb/in
|
ASTM D256, ISO 180 |
|
Deflection Temperature Under Load (264 psi, Unannealed)
|
|
°F
|
ASTM D648, ISO 75-2/A |
|
Vicat Softening Temperature
|
|
°F
|
ISO 306/B50, ASTM D1525 3 |
|
Ball Pressure Test (473°F)
|
|
|
VDE 0470 |
|
Melting Temperature
|
|
°F
|
ASTM D211, ISO 121 |
|
CLTE - Flow (-22 to 86°F)
|
|
in/in/°F
|
ASTM D696 |
|
Dielectric Strength (0.0394 in)
|
|
V/mil
|
ASTM D149 |
|
Comparative Tracking Index (Solution A)
|
|
V
|
IEC 60112 |
|
Flame Rating - UL (0.0382 in)
|
|
|
UL 94 |
|
Glow Wire Ignition Temperature (0.0787 in)
|
|
°F
|
IEC 60695-2-13 |
|
Oxygen Index
|
|
%
|
ASTM D2863 |
|
Grafted Base Resin
|
|
%
|
Internal Method |
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: TAROLOX 111 G5, TAROLOX , TAROLOX111G5, 111 G 5, 111 G5, 111G, G5, 111G5, Polyethylene Terephthalate, PET, Polyester, Taro Plast, PolyethyleneTerephthalate, G111
|
|
Features may also be described by the following terms: High Heat Resistance, Good Chemical Resistance, Chemical Resistant, Good Electrical Properties, Low Moisture Absorption, Low Water Absorption, Water Resistant, Moisture Resistant, Good Dimensional Stability, Dimensionally Stable.
|