Specific Gravity
|
|
|
|
|
--
|
|
|
ASTM D792 |
|
--
|
|
g/cm³
|
ISO 1183 |
|
Melt Mass-Flow Rate (MFR) (280°C/1.0 kg)
|
|
g/10 min
|
ASTM D1238, ISO 1133 |
|
Molding Shrinkage
|
|
|
ASTM D955 |
|
Flow
|
|
in/in
|
|
|
Across Flow
|
|
in/in
|
|
|
Water Absorption
|
|
|
|
|
73°F, 24 hr
|
|
%
|
ASTM D570, ISO 62 |
|
Saturation
|
|
%
|
ASTM D570 |
|
Saturation, 73°F
|
|
%
|
ISO 62 |
|
Tensile Modulus
|
|
psi
|
ASTM D638, ISO 527-2 |
|
Tensile Strength (Break)
|
|
psi
|
ASTM D638, ISO 527-2 |
|
Tensile Elongation (Break)
|
|
%
|
ASTM D638, ISO 527-2 |
|
Flexural Modulus
|
|
psi
|
ASTM D790, ISO 178 |
|
Flexural Strength
|
|
|
|
|
--
|
|
psi
|
ISO 178 |
|
Break
|
|
psi
|
ASTM D790 |
|
Charpy Notched Impact Strength (73°F)
|
|
ft·lb/in²
|
ISO 179 |
|
Notched Izod Impact (73°F, 0.126 in)
|
|
ft·lb/in
|
ASTM D256 |
|
Rockwell Hardness (R-Scale)
|
|
|
ASTM D785 |
|
Deflection Temperature Under Load (264 psi, Unannealed)
|
|
°F
|
ASTM D648, ISO 75-2/A |
|
Max. Continuous Use Temperature
|
|
°F
|
ASTM D794 |
|
Vicat Softening Temperature
|
|
°F
|
ISO 306/B50, ASTM D1525 2 |
|
Melting Temperature
|
|
°F
|
|
|
CLTE - Flow (-22 to 86°F)
|
|
in/in/°F
|
ASTM D696 |
|
Volume Resistivity
|
|
ohm·cm
|
ASTM D257 |
|
Dielectric Strength (0.0787 in)
|
|
V/mil
|
ASTM D149 |
|
Flame Rating - UL (0.0630 in)
|
|
|
UL 94 |
|
Oxygen Index
|
|
%
|
ASTM D2863 |
|
Granule Humidity, TARO 002: <0.15%
Spiral Flow, TARO 003, 280°C - 60°C: 320
Ball Pressure Test, VDE 0470: 165°C
Continuous Service Temperature, IEC 216, 130 hr: 100°C
Continuous Service Temperature, IEC 216, 180 hr, short term: 140°C
Density, ISO 118: 1.36 to 1.38 Mg/m³
Density. ASTM D792: 1.36 to 1.38 Mg/m³
Notched Izod Impact Strength , ISO 180, 23°C: 110 J/m
Charpy Impact Strength, ASTM D256, 23°C, 4mm: 7.8 kJ/m²
|
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: TAROMID A 280 G6 MB1, TAROMID A , TAROMIDA280G6MB1, TAROMIDA, A 280 G 6 MB 1, A280 G6 MB1, A280, 280 G 6 MB 1, A280G6MB1, 280 G6 MB1, 280G, G6, 6MB, MB1, 280G6MB1, Polyamide 66, Nylon 66, Polyamide, Nylon, pa66, Taro Plast, Polyamide66, Nylon66, G280, 280A
|
|
Generic Name may also be described by the following terms: PA66.
|
|
Features may also be described by the following terms: Medium Viscosity, Heat Stabilized, Heat-ageing Stabilized, Heat Ageing Stabilized, Heat-aging Stabilized, Heat Aging Stabilized, Good Mold Release, Easy Release, Good Demolding, Low Friction.
|