Specific Gravity
|
|
|
|
|
--
|
|
|
ASTM D792 |
|
--
|
|
g/cm³
|
ISO 1183 |
|
Melt Mass-Flow Rate (MFR) (280°C/1.2 kg)
|
|
g/10 min
|
ASTM D1238, ISO 1133 |
|
Molding Shrinkage
|
|
|
ASTM D955 |
|
Flow
|
|
in/in
|
|
|
Across Flow
|
|
in/in
|
|
|
Water Absorption
|
|
|
|
|
73°F, 24 hr
|
|
%
|
ASTM D570, ISO 62 |
|
Saturation
|
|
%
|
ASTM D570 |
|
Saturation, 73°F
|
|
%
|
ISO 62 |
|
Granule Humidity
|
|
%
|
Internal Method |
|
Tensile Modulus
|
|
psi
|
ASTM D638, ISO 527-2 |
|
Tensile Strength
|
|
|
ASTM D638, ISO 527-2 |
|
Yield
|
|
psi
|
|
|
Break
|
|
psi
|
|
|
Tensile Elongation (Break)
|
|
%
|
ASTM D638, ISO 527-2 |
|
Flexural Modulus
|
|
psi
|
ASTM D790, ISO 178 |
|
Flexural Strength
|
|
|
|
|
--
|
|
psi
|
ISO 178 |
|
Yield
|
|
psi
|
ASTM D790 |
|
Charpy Notched Impact Strength 2 (73°F)
|
|
ft·lb/in²
|
ASTM D256, ISO 179 |
|
Charpy Unnotched Impact Strength 2 (73°F)
|
|
ft·lb/in²
|
ASTM D256, ISO 179 |
|
Notched Izod Impact
|
|
|
|
|
-4°F, 0.126 in
|
|
ft·lb/in
|
ISO 180, ASTM D256 |
|
73°F, 0.126 in
|
|
ft·lb/in
|
ASTM D256, ISO 180 |
|
Rockwell Hardness (R-Scale)
|
|
|
ASTM D785 |
|
Deflection Temperature Under Load (264 psi, Unannealed)
|
|
°F
|
ASTM D648, ISO 75-2/A |
|
Max. Continuous Use Temperature
|
|
|
IEC 60216 |
|
-- 3
|
|
°F
|
|
|
-- 4
|
|
°F
|
|
|
Vicat Softening Temperature
|
|
|
|
|
--
|
|
°F
|
ASTM D1525 5, ISO 306/A50 5 |
|
--
|
|
°F
|
ASTM D1525 6, ISO 306/B50 6 |
|
Ball Pressure Test (329°F)
|
|
|
VDE 0470 |
|
Melting Temperature
|
|
°F
|
ASTM D211, ISO 121 |
|
CLTE - Flow (-22 to 86°F)
|
|
in/in/°F
|
ASTM D696 |
|
Volume Resistivity
|
|
ohm·cm
|
ASTM D257 |
|
Dielectric Strength (0.0787 in)
|
|
V/mil
|
ASTM D149 |
|
Comparative Tracking Index
|
|
|
IEC 60112 |
|
Solution A
|
|
V
|
|
|
Solution B
|
|
V
|
|
|
Flame Rating - UL (0.0630 in)
|
|
|
UL 94 |
|
Glow Wire Ignition Temperature (0.0787 in)
|
|
°F
|
IEC 60695-2-13 |
|
Oxygen Index
|
|
%
|
ASTM D2863 |
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: TAROMID A 280S, TAROMID A , TAROMIDA280S, TAROMIDA, A 280 S, A280S, A280, 280 S, 280S, Polyamide 66, Nylon 66, Polyamide, Nylon, pa66, Taro Plast, Polyamide66, Nylon66, S280, 280A
|
|
Generic Name may also be described by the following terms: PA66.
|
|
Features may also be described by the following terms: Medium Viscosity, Good Processability, Easy Processing, Good Mold Release, Easy Release, Good Demolding, Low Shrinkage, Good Dimensional Stability, Dimensionally Stable, Fast Cycle, Rapid Cycle, Productivity, Fast Molding Cycle, High Rigidity.
|