Reaction between grafting and catalyst, must be mixed before starting extrusion in the ratio, Grafting/Catalyst: 95/5 Temperature Index, 21% O2: >300°C HCI Generation: 0% Melt Flow Rate, ASTM D1238, 190°C/21.6 kg: 8 to 12 g/10min Hot Set Test, reading after 15, IEC 540, 20 N/cm² at 200°C: 50% Hot Set Test, residual value, IEC 540, 20 N/cm² at 200°C: 0% Crosslinking of the finished product is obtained by:
- Immersion of the bobbin in hot water at 85/90°C for two hours up to 3 mm thickness
- Steam treatment at 0.15 bar for 5/6 hours
- Air crosslinking at natural temperatures and moisture: in progress
Reaction between grafting and catalyst, must be mixed before starting extrusion in the ratio, Grafting/Catalyst: 95/50 |
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: FRAGOM G/320-C, FRAGOM G320C, FRAGOM , FRAGOMG320C, G 320 C, G/320-C, G320C, G:320-C, G+320-C, G-320-C, G_320-C, G 320-C, G/320:C, G/320/C, G/320+C, G/320_C, G/320 C, G320, 320C, G_320C, G 320C, G320_C, G320 C, Polyolefin, Unspecified, Polyolefin Unspecified, Polyolefin, Crosspolimeri, PolyolefinUnspecified, 320G
|