GETILAN ATP/130-XH

Reaction between grafting and catalyst, must be mixed before starting extrusion in the ratio, Grafting/Catalyst: 95/5
Compression Set, 1000h, 4.4 Mpa, 95°C: pass
Compression Set, 1h, 4.8 Mpa, 95°C: pass
Melt Flow Rate, ASTM D1238, 190°C/5 kg: 0.3 to 1 g/10min
Crosslinking of the finished product is obtained by:

• Immersion of the bobbin in hot water at 85/90°C for two hours up to 3 mm thickness

• Steam treatment at 0.15 bar for 5/6 hours

Reaction between grafting and catalyst, must be mixed before starting extrusion in the ratio, Grafting/Catalyst: 95/50
Compression Set, 1000h, 4.4 Mpa, 95°C: pass

Product names can be difficult to match. You may have searched any one of these terms to find this product: GETILAN ATP/130-XH, GETILAN ATP130XH, GETILAN , GETILANATP130XH, ATP, ATP 130 XH, ATP/130-XH, ATP130XH, ATP:130-XH, ATP+130-XH, ATP-130-XH, ATP_130-XH, ATP 130-XH, ATP/130:XH, ATP/130/XH, ATP/130+XH, ATP/130_XH, ATP/130 XH, ATP130, 130XH, ATP_130XH, ATP 130XH, ATP130_XH, ATP130 XH, Polyethylene, Crosslinked, Polyethylene Crosslinked, XLPE, Polyethylene, PE, Crosspolimeri, PolyethyleneCrosslinked, 130ATP

Uses may also be described by the following terms: Fiber Optic Cable, Fiber Optics.

The extrusion parameters listed are for 18 mm pipe.
22 mm pipe:

• Zone 1 Temperature: 160°C

• Zone 2 Temperature: 170°C

• Zone 3 Temperature: 185°C

• Zone 4 Temperature: 190°C

• Head Temperature: 195°C

• Die Temperature: 200°C