GETILAN ATP/130-XU

Reaction between grafting and catalyst, must be mixed before starting extrusion in the ratio, Grafting/Catalyst: 95/5
Compression Set, 1000h, 4.4 Mpa, 95°C: pass
Compression Set, 1h, 4.8 Mpa, 95°C: pass
Melt Flow Rate, ASTM D1238, 190°C/5 kg: 0.5 to 3 g/10min
Crosslinking of the finished product is obtained by:

• Immersion of the bobbin in hot water at 85/90°C for two hours up to 3 mm thickness

• Steam treatment at 0.15 bar for 5/6 hours

Reaction between grafting and catalyst, must be mixed before starting extrusion in the ratio, Grafting/Catalyst: 95/50
Compression Set, 1000h, 4.4 Mpa, 95°C: pass

Product names can be difficult to match. You may have searched any one of these terms to find this product: GETILAN ATP/130-XU, GETILAN ATP130XU, GETILAN , GETILANATP130XU, ATP, ATP 130 XU, ATP/130-XU, ATP130XU, ATP:130-XU, ATP+130-XU, ATP-130-XU, ATP_130-XU, ATP 130-XU, ATP/130:XU, ATP/130/XU, ATP/130+XU, ATP/130_XU, ATP/130 XU, ATP130, 130XU, ATP_130XU, ATP 130XU, ATP130_XU, ATP130 XU, Polyethylene, Crosslinked, Polyethylene Crosslinked, XLPE, Polyethylene, PE, Crosspolimeri, PolyethyleneCrosslinked, 130ATP

Features may also be described by the following terms: High Density, High Specific Gravity.

Uses may also be described by the following terms: Piping, Pipe.

The extrusion parameters listed are for 18 mm pipe.
22 mm pipe:

• Zone 1 Temperature: 175°C

• Zone 2 Temperature: 180°C

• Zone 3 Temperature: 185°C

• Zone 4 Temperature: 195°C

• Head Temperature: 210°C

• Die Temperature: 215 to 225°C