ATTANE™ 4607G

Ultra Low Density Polyethylene Resin

Supplied by The Dow Chemical Company

The technical datasheet with complete property values for ATTANE™ 4607G is available to members of the Prospector Plastics Database.
Register to view full datasheet.
Register to View Full Datasheet
Product Description
ATTANE™ 4607G Ultra Low Density Polyethylene Copolymer as a skin layer in cast film offers excellent low temperature hot tack properties combined with outstanding tear and impact strength. In stretch film applications, ATTANE™ 4607G Ultra Low Density Polyethylene Copolymer exhibits excellent stretchability as well as good physical and cling properties. ATTANE™ 4607G Ultra Low Density Polyethylene Copolymer can also be utilised in blown film coextrusion where it is combined with other resins having excellent bubble stability allowing ATTANE™ 4607G Ultra Low Density Polyethylene Copolymer to be used as a sealant in multilayer film structures.

Applications:
  • Cling layer in cast stretch film
  • Sealants in cast and blown films

Complies with:
  • EU, No 10/2011
  • U.S. FDA FCN 741
Consult the regulations for complete details.
General  
Material Status 
  • Commercial: Active
Availability 
  • Europe
Agency Ratings 
 
Forms 
  • Pellets
Processing Method 
  • Cast Film
Physical
Nominal Value
Unit
Test Method
Specific Gravity
 
 ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)
g/10 min
 ISO 1133
Films
Nominal Value
Unit
Test Method
Film Thickness - Tested
mil
  
Film Puncture Energy (0.91 mil)
in·lb
 Internal Method
Film Puncture Force (0.91 mil)
lbf
 Internal Method
Tensile Stress
     ISO 527-3
MD: Yield, 0.91 mil
psi
  
TD: Yield, 0.91 mil
psi
  
MD: Break, 0.91 mil
psi
  
TD: Break, 0.91 mil
psi
  
Tensile Elongation
     ISO 527-3
MD: Break, 0.91 mil
%
  
TD: Break, 0.91 mil
%
  
Dart Drop Impact (0.91 mil)
g
 ISO 7765-1/A
Elmendorf Tear Strength
     ASTM D1922
MD: 0.91 mil
g
  
TD: 0.91 mil
g
  
Unstretched Cling
g
 ASTM D4649
Thermal
Nominal Value
Unit
Test Method
Vicat Softening Temperature
°F
 ISO 306/A
Optical
Nominal Value
Unit
Test Method
Gloss (45°, 0.906 mil)
 
 ASTM D2457
Haze (0.906 mil)
%
 ASTM D1003
Additional Information
Film properties measured on monolayer film produced on a Lab Collin line 15 m/min chill roll 25°C.
Related Terminology
Product names can be difficult to match. You may have searched any one of these terms to find this product: ATTANE™ 4607G, ATTANE 4607G, ATTANE™ , ATTANE, ATTANE4607G, 4607 G, 4607G, Polyethylene, Ultra Low Density, Polyethylene Ultra Low Density, ULDPE, Polyethylene, PE, Dow, PolyethyleneUltraLowDensity, G4607
Agency Ratings
This plastic material has 2 certifications from the following agencies (the number in parentheses shows the number of certifications for that agency): EU (1), FDA (1).
Extrusion
Nominal Value
Unit
 
Melt Temperature
°F
  
Extrusion Notes
Fabrication Conditions For Cast Film Extrusion:
  • Melt Temperature: 190 - 260 °C
  • Recommended Gauge Range: 10 - 60 µm
  • Haul-Off Speed: 150 - 300 m/min
  • Chill Roll Temperature: 20 - 60 °C
Notes
1Typical properties: these are not to be construed as specifications.
 
IDES
Copyright © 2012 IDES
The information presented on this datasheet was acquired by IDES from the producer of the material. IDES makes substantial efforts to assure the accuracy of this data. However, IDES assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.