PALMID R 6 S GF 10 MV 20 pal plast Polyamide 6 (Glass Fiber Reinforcement, 10%; Mineral Filler, 20%)

General

Material Status

Commercial: Active

Availability

Europe

Filler / Reinforcement

Glass Fiber Reinforcement, 10% Filler by Weight

Mineral Filler, 20% Filler by Weight

Features

Good Dimensional Stability

Good Stiffness

Low Warpage

Uses

Housings

Forms

Pellets

Processing Method

Injection Molding

Physical	Nominal Value	Unit	Test Method
Density		g/cm³	ISO 1183
Water Absorption			ISO 62
Saturation, 73°F		%
Equilibrium, 73°F, 50% RH		%
Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (73°F)		psi	ISO 527-2/1A/1
Tensile Stress (Break, 73°F)		psi	ISO 527-2/1A/5
Tensile Strain (Break, 73°F)		%	ISO 527-2/1A/5
Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (73°F)		ft·lb/in²	ISO 179/1eA
Charpy Unnotched Impact Strength (73°F)		ft·lb/in²	ISO 179/1eU
Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature		°F	ISO 306/B50
Melting Temperature (DSC)		°F	ISO 3146
Flammability	Nominal Value	Unit	Test Method
Flame Rating - UL (0.0630 in)			UL 94
Additional Information
Tensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 5800 to 6300 MPa Tensile Stress at Break, ISO 527, 23°C, 5 mm/min, Type A: 100 to 120 MPa Tensile Strain at Break, ISO 527, 23°C, 5 mm/min, Type A: 3 to 4 % Charpy Unnotched Impact, ISO 179, Type 1, Edgewise, 23°C: 30 to 40 kJ/m² Charpy Notched Impact, ISO 179, Type 1, Edgewise, Notch A, 23°C: 4 to 6 kJ/m² Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 205 to 209 °C Density, ISO 1183: 1.34 to 1.36 g/cm³ Water Absorption, ISO 62, 23°C, Saturation: 6.1 to 6.3 % Moisture Absorption, ISO 62, 23°C, 50% RH: 1.6 to 1.8 %
Related Terminology
Product names can be difficult to match. You may have searched any one of these terms to find this product: PALMID® R 6 S GF 10 MV 20, PALMID R 6 S GF 10 MV 20, PALMID® , PALMID, PALMIDR6SGF10MV20, R 6 S GF 10 MV 20, R6, 6S, SGF, GF10, 10MV, MV20, R6SGF10MV20, Polyamide 6, Nylon 6, Polyamide, Nylon, pa6, pal plast, Polyamide6, Nylon6, 6R
Generic Name
Generic Name may also be described by the following terms: PA6.
Features
Features may also be described by the following terms: Good Stiffness, Low Warpage, Low Warp, Good Dimensional Stability, Dimensionally Stable.
Uses
Uses may also be described by the following terms: Housings, Housing.

Notes

¹Typical properties: these are not to be construed as specifications.

PALMID® R 6 S GF 10 MV 20

Polyamide 6

Glass Fiber Reinforcement, 10%; Mineral Filler, 20%

Supplied by pal plast GmbH