PALGLAS® R 08

Tensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 3000 to 3200 MPa
Tensile Stress at Break, ISO 527, 23°C, 5 mm/min, Type A: 72 to 77 MPa
Tensile Strain at Break, ISO 527, 23°C, 5 mm/min, Type A: 4 to 6 %
Charpy Unnotched Impact, ISO 179, Type 1, Edgewise, 23°C: 15 to 20 kJ/m²
Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 105 to 108 °C
Density, ISO 1183: 1.18 to 1.2 g/cm³
Water Absorption, ISO 62, 23°C, Saturation: 1.9 to 2.1 %
Moisture Absorption, ISO 62, 23°C, 50% RH: 0.5 to 0.7 %

Product names can be difficult to match. You may have searched any one of these terms to find this product: PALGLAS® R 08, PALGLAS R 08, PALGLAS® , PALGLAS, PALGLASR08, R 08, R08, Acrylic, Acrylic, Polymethyl Methacrylate, Acrylic Polymethyl Methacrylate, Acrylic (PMMA), Acrylic PMMA, pmma, pal plast, AcrylicPolymethylMethacrylate, AcrylicPMMA, 08R

Features may also be described by the following terms: High Heat Resistance, High Hardness, Hard, High Clarity.

Uses may also be described by the following terms: Automotive Applications, Automotive Sector.