Melt-Volume Flow Rate, ISO 1133, 230°C/2.16 kg: 15 to 25 cm³/10 min
Tensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 1350 to 1500 MPa
Tensile Stress at Yield, ISO 527, 23°C, 50 mm/min, Type A: 30 to 34 MPa
Tensile Strain at Yield, ISO 527, 23°C, 50 mm/min, Type A: 6 to 8 %
Nominal Tensile Strain at Break, ISO 527, 23°C, 50 mm/min, Type A: >50 %
Charpy Unnotched Impact, ISO 179, Type 1, Edgewise, 23°C: 85 to 95 kJ/m²
Charpy Notched Impact, ISO 179, Type 1, Edgewise, Notch A, 23°C: 2 to 3 kJ/m²
Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 80 to 85 °C
Density, ISO 1183: 0.9 to 0.91 g/cm³
|
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: PALPROP® R H 20, PALPROP R H 20, PALPROP® , PALPROP, PALPROPRH20, R H 20, RH, H20, RH20, Polypropylene Homopolymer, PP Homopolymer, Polypropylene, PP, pal plast, PolypropyleneHomopolymer, PPHomopolymer, HR
|