PALDUR® R 15 GK 20

Tensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 3300 to 3700 MPa
Tensile Stress at Break, ISO 527, 23°C, 5 mm/min, Type A: 48 to 53 MPa
Tensile Strain at Break, ISO 527, 23°C, 5 mm/min, Type A: 4 to 6 %
Charpy Notched Impact, ISO 179, Type 1, Edgewise, Notch A, 23°C: 3 to 5 kJ/m²
Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 187 to 190 °C
Density, ISO 1183: 1.44 to 1.46 g/cm³
Water Absorption, ISO 62, 23°C, Saturation: 0.35 to 0.4 %
Moisture Absorption, ISO 62, 23°C, 50% RH: 0.12 to 0.15 %

Product names can be difficult to match. You may have searched any one of these terms to find this product: PALDUR® R 15 GK 20, PALDUR R 15 GK 20, PALDUR® , PALDUR, PALDURR15GK20, R 15 GK 20, R15, 15GK, GK20, R15GK20, Polybutylene Terephthalate, PBT, Polyester, pal plast, PolybutyleneTerephthalate, 15R