XYLEX* X7519HP Resin

Polycarbonate + Polyester

Supplied by SABIC Innovative Plastics

The technical datasheet with complete property values for XYLEX* X7519HP Resin is available to members of the Prospector Plastics Database.
Register to view full datasheet.
Register to View Full Datasheet
Product Description
Good Chemical Resistance, XYLEX grade with good dishwasher performance, USA/Europe Food Contact Comment: While molding of thicker parts, cooling speed has an influence of transparency. Thicker parts may form opaque areas in the centre due to slow cooling.
General  
Material Status 
  • Commercial: Active
Availability 
  • North America
Features 
  • Food Contact Acceptable
  • Good Chemical Resistance
  
Processing Method 
  • Injection Molding
Physical
Nominal Value
Unit
Test Method
Specific Gravity
      
--
 
 ASTM D792
--
g/cm³
 ISO 1183
Melt Mass-Flow Rate (MFR) (300°C/1.2 kg)
g/10 min
 ASTM D1238
Melt Volume-Flow Rate (MVR) (300°C/1.2 kg)
in³/10min
 ISO 1133
Molding Shrinkage - Flow (0.126 in)
in/in
 Internal Method
Water Absorption
     ISO 62
Saturation, 73°F
%
  
Equilibrium, 73°F, 50% RH
%
  
Mechanical
Nominal Value
Unit
Test Method
Tensile Modulus
      
-- 2
psi
 ASTM D638
--
psi
 ISO 527-2/1
Tensile Strength
      
Yield 3
psi
 ASTM D638
Yield
psi
 ISO 527-2/50
Break 3
psi
 ASTM D638
Break
psi
 ISO 527-2/50
Tensile Elongation
      
Yield 3
%
 ASTM D638
Yield
%
 ISO 527-2/50
Break 3
%
 ASTM D638
Break
%
 ISO 527-2/50
Flexural Modulus
      
1.97 in Span 4
psi
 ASTM D790
-- 5
psi
 ISO 178
Flexural Strength
      
-- 5, 6
psi
 ISO 178
Yield, 1.97 in Span 4
psi
 ASTM D790
Impact
Nominal Value
Unit
Test Method
Charpy Notched Impact Strength 7 (73°F)
ft·lb/in²
 ISO 179/1eA
Notched Izod Impact
      
-22°F
ft·lb/in
 ASTM D256
73°F
ft·lb/in
 ASTM D256
-22°F 8
ft·lb/in²
 ISO 180/1A
73°F 8
ft·lb/in²
 ISO 180/1A
Instrumented Dart Impact (73°F, Total Energy)
in·lb
 ASTM D3763
Thermal
Nominal Value
Unit
Test Method
Deflection Temperature Under Load
      
264 psi, Unannealed, 0.126 in
°F
 ASTM D648
264 psi, Unannealed, 2.52 in Span 9
°F
 ISO 75-2/Af
Vicat Softening Temperature
      
--
°F
 ASTM D1525 10, ISO 306/B50 10
--
°F
 ISO 306/B120
CLTE
      
Flow: -40 to 104°F
in/in/°F
 ASTM E831
Flow: -40 to 104°F
in/in/°F
 ISO 11359-2
Transverse: -40 to 104°F
in/in/°F
 ASTM E831
Transverse: -40 to 104°F
in/in/°F
 ISO 11359-2
Related Terminology
This supplier and product may also be known by these terms: GE Plastics, LNP Engineering Plastics, GE Polymerland

Product names can be difficult to match. You may have searched any one of these terms to find this product: XYLEX* X7519HP Resin, XYLEX X7519HP Resin, XYLEX* , XYLEX, XYLEXX7519HPResin, X 7519 HP Resin, X7519HP Resin, X7519, 7519HP, HPResin, X7519HPResin, Polycarbonate + Polyester, Polycarbonate Polyester, Polycarbonate : Polyester, Polycarbonate / Polyester, Polycarbonate - Polyester, Polycarbonate _ Polyester, Polycarbonate Polyester, PC+Polyester, PCPolyester, PC:Polyester, PC/Polyester, PC-Polyester, PC_Polyester, PC Polyester, Polycarbonate, PC, SABIC IP, PolycarbonatePolyester, Polycarbonate_Polyester, 7519X
Features
Features may also be described by the following terms: Good Chemical Resistance, Chemical Resistant.
Injection
Nominal Value
Unit
 
Drying Temperature
°F
  
Drying Time
hr
  
Drying Time, Maximum
hr
  
Suggested Max Moisture
%
  
Suggested Shot Size
%
  
Hopper Temperature
°F
  
Rear Temperature
°F
  
Middle Temperature
°F
  
Front Temperature
°F
  
Nozzle Temperature
°F
  
Processing (Melt) Temp
°F
  
Mold Temperature
°F
  
Back Pressure
psi
  
Screw Speed
rpm
  
Notes
1Typical properties: these are not to be construed as specifications.
20.20 in/min
3Type I, 2.0 in/min
40.051 in/min
50.079 in/min
6Yield
780*10*4 sp=62mm
880*10*4
980*10*4 mm
10Rate B (120°C/h), Loading 2 (50 N)
 
IDES
Copyright © 2012 IDES
The information presented on this datasheet was acquired by IDES from the producer of the material. IDES makes substantial efforts to assure the accuracy of this data. However, IDES assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.