NOVALAC RX®611V Vyncolit Phenolic (Glass Fiber Reinforcement)

General

Material Status

Availability

Filler / Reinforcement

Features

Uses

Forms

Processing Method

Physical	Nominal Value	Unit	Test Method
Density		g/cm³	ISO 1183
Molding Shrinkage - Flow		%	ISO 294-4
Water Absorption (73°F, 24 hr)		%	ISO 62
Mechanical	Nominal Value	Unit	Test Method
Tensile Stress (Break)		psi	ISO 527-2
Flexural Modulus		psi	ISO 178
Flexural Strength		psi	ISO 178
Impact	Nominal Value	Unit	Test Method
Notched Izod Impact Strength		ft·lb/in²	ISO 180
Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (E-Scale)			ISO 2039-2
Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (264 psi, Unannealed)		°F	ISO 75-2/A
CLTE - Flow		in/in/°F	ASTM D696
Thermal Conductivity		Btu·in/hr/ft²/°F	ASTM C177
Electrical	Nominal Value	Unit	Test Method
Arc Resistance		sec	ASTM D495
Electric Strength		V/mil	IEC 60243-1
Related Terminology
Product names can be difficult to match. You may have searched any one of these terms to find this product: NOVALAC RX®611V, NOVALAC RX611V, NOVALAC , NOVALACRX611V, RX 611 V, RX®611V, RX611V, RX611, 611V, Phenolic, Vyncolit, 611RX
Features
Features may also be described by the following terms: Ultra High Toughness, High Strength, Low Smoke Emission, Good Dimensional Stability, Dimensionally Stable, Good Creep Resistance, Creep Resistant.
Uses
Uses may also be described by the following terms: Power Tools, Tools, Membrane Touch Switches, Housings, Housing, Electrical Applications, Electronic Applications, Electrical/Electronic Applications, Electrical Sector, Automotive Applications, Automotive Sector.

Injection	Nominal Value	Unit
Rear Temperature		°F
Middle Temperature		°F
Nozzle Temperature		°F
Processing (Melt) Temp		°F
Mold Temperature		°F
Back Pressure		psi
Injection Notes
Plastication: 50rpm Injection Pressure: Set to give 3 to 5 seconds injection time Hold Pressure: 50 to 100% of injection pressure Hold Time: 10 sec minimum Cure Time, 0.125 in: 30 to 35 sec The value listed as Thermal Conductivity, ASTM C177, was tested in accordance with ASTM C518. The value listed as Molding Shrinkage, ISO 294-4, was tested in accordance with ISO 2577 using compression molded specimens. Compressive Strength, ISO 604: 320 MPa Dielectric Strength, IEC 243, Method A, wet: 10 V/mil Compression and Transfer Molding Conditions: Preforming Pressure: 8000 to 12000 psi Preheat Temperature: 210 to 235 °F Preheat Time: 45 sec Mold Temperature: 330 to 360 °F Compression Mold Pressure: 2500 to 5000 psi Transfer Mold Pressure: 4000 to 6000 psi Cure Time, 0.125 in: 40 to 50 sec

Notes

¹Typical properties: these are not to be construed as specifications.

NOVALAC RX®611V