Specific Gravity
|
|
|
|
|
--
|
|
|
ASTM D792 |
|
--
|
|
g/cm³
|
ISO 1183 |
|
Molding Shrinkage
|
|
|
|
|
Flow: 0.126 in
|
|
in/in
|
ASTM D955 |
|
Across Flow: 0.126 in
|
|
in/in
|
ASTM D955 |
|
Across Flow: 0.126 in
|
|
%
|
ISO 294-4 |
|
Flow: 0.126 in
|
|
%
|
ISO 294-4 |
|
Water Absorption
|
|
|
ASTM D570 |
|
24 hr
|
|
%
|
|
|
Saturation
|
|
%
|
|
|
Tensile Strength (Yield)
|
|
psi
|
ASTM D638, ISO 527-2 |
|
Tensile Elongation (Break)
|
|
%
|
ASTM D638, ISO 527-2 |
|
Flexural Modulus
|
|
psi
|
ASTM D790, ISO 178 |
|
Flexural Strength
|
|
|
|
|
--
|
|
psi
|
ISO 178 |
|
Yield
|
|
psi
|
ASTM D790 |
|
Notched Izod Impact
|
|
ft·lb/in
|
ASTM D256 |
|
Deflection Temperature Under Load
|
|
|
|
|
66 psi, Unannealed
|
|
°F
|
ASTM D648, ISO 75-2/B |
|
264 psi, Unannealed
|
|
°F
|
ASTM D648, ISO 75-2/A |
|
Vicat Softening Temperature
|
|
|
|
|
--
|
|
°F
|
ASTM D1525 2 |
|
--
|
|
°F
|
ASTM D1525 3 |
|
--
|
|
°F
|
ISO 306 |
|
Melting Temperature
|
|
°F
|
|
|
CLTE - Flow (-22 to 86°F)
|
|
in/in/°F
|
ASTM D696, ISO 11359-2 |
|
Thermal Conductivity
|
|
Btu·in/hr/ft²/°F
|
ASTM C177, ISO 8302 |
|
Surface Resistivity
|
|
ohms
|
ASTM D4496, IEC 60093 |
|
Volume Resistivity
|
|
ohm·cm
|
ASTM D257, IEC 60093 |
|
Dielectric Strength
|
|
V/mil
|
ASTM D149, IEC 60243-1 |
|
Comparative Tracking Index (Solution A)
|
|
V
|
IEC 60112 |
|
Flame Rating - UL (0.126 in)
|
|
|
UL 94 |
|
Glow Wire Flammability Index (0.0394 in)
|
|
°F
|
IEC 60695-2-12 |
|
Oxygen Index
|
|
%
|
ASTM D2863 |
|
Notched Izod Impact, ISO 11357-3: 45 J/m
Ball Test, IEC 335-1, 125°C-165°Cs/s
Service Temperature, 20.000 h: 120°C
Service Temperature, IEC 216, Short Term: 160°C
Comparative Tracking Index, IEC 212, Solution B: 350M V
|
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: GREENOX NAT, GREENOX , GREENOXNAT, NAT, Polybutylene Terephthalate, PBT, Polyester, Plastigreen, PolybutyleneTerephthalate
|
|
Features may also be described by the following terms: Good Surface Finish, Good Flow.
|