The value listed as Specific Gravity, ASTM D792, was tested in accordance with ASTM D471.
The value listed as Density, ISO 1183, was tested in accordance with ISO 2781.
The value listed as Shore Hardness, ISO 868, was tested in accordance with ISO 48.
Permanent Set (Tension), ASTM D412, Compression Molding, 1.9 mm: 17%
100% Modulus, ASTM D412, ISO 37, Physical Retention After 7 Days at 125°C, Compression Molding, 1.9 mm: 148%
Tensile Strength, ASTM D412, ISO 37, DIN 53504, Physical Retention After 7 Days at 125°C, Compression Molding, 1.9 mm: 112%
Elongation At Break, ASTM D412, ISO 37, Physical Retention After 7 Days at 125°C, Compression Molding, 1.9 mm: 1106%
Hardness, ISO 48, Physical Retention After 7 Days at 125°C, Shore A, Compression Molding, 1.9 mm: 77
Viscosity, ASTM D3835, 300 s-1 at 190°C, Compression Molding, 1.9 mm: 430 Pa*s
Typical Processing Temperature, Compression Molding, 1.9 mm: 177° C
Volume Change, ASTM D471, ISO 1817, After 7 days, 100°C, Water, Compression Molding, 1.9 mm: 12%
Volume Change, After 7 days,ASTM D471, ISO 1817, 24°C, Fuel B, Compression Molding, 1.9 mm: 26%
Volume Change, After 7 days, ASTM D471, ISO 1817, 100°C, ASTM #1 Oil, Compression Molding, 1.9 mm: -6%
Volume Change, After 7 days, ASTM D471, ISO 1817, 100°C, IRM 903 Oil #3, Compression Molding, 1.9 mm: 16%
Clash-Berg Stiffness Temperature, ASTM D1043, 10000 psi, Compression Molding, 1.9 mm: -19° C
|
|
This supplier and product may also be known by these terms: APA, Advanced Polymer Alloys is a division of Ferro
Product names can be difficult to match. You may have searched any one of these terms to find this product: Alcryn® 2180 BK, Alcryn 2180 BK, Alcryn® , Alcryn, Alcryn2180BK, 2180 BK, 2180BK, Melt Processable Rubber, MPR, Thermoplastic Elastomer, TPE, APA, MeltProcessableRubber, ThermoplasticElastomer, BK2180
|