DUCTEL C9704 Nanjing Lihan Chemical Co., Ltd. Polycarbonate (Glass Fiber Reinforcement, 20%)

General
Material Status	Commercial: Active
Availability	Asia Pacific
Filler / Reinforcement	Glass Fiber Reinforcement, 20% Filler by Weight
Features	Flame Retardant
Uses	Electrical Parts
Forms	Pellets

Physical	Nominal Value	Unit	Test Method
Specific Gravity
--			ASTM D792
--		g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (300°C/1.2 kg)		g/10 min	ASTM D1238, ISO 1133
Molding Shrinkage - Flow		in/in	ASTM D955
Water Absorption
24 hr		%	ASTM D570
73°F, 24 hr		%	ISO 62
Equilibrium		%	ASTM D570
Equilibrium, 73°F, 50% RH		%	ISO 62
Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Break)		psi	ASTM D638, ISO 527-2
Tensile Elongation (Break)		%	ASTM D638, ISO 527-2
Flexural Modulus		psi	ASTM D790, ISO 178
Flexural Strength
--		psi	ISO 178
Yield		psi	ASTM D790
Impact	Nominal Value	Unit	Test Method
Notched Izod Impact Strength		ft·lb/in²	ISO 180
Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (R-Scale)			ISO 2039-2
Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load
66 psi, Unannealed		°F	ASTM D648, ISO 75-2/B
264 psi, Unannealed		°F	ASTM D648, ISO 75-2/A
Electrical	Nominal Value	Unit	Test Method
Surface Resistivity		ohms	ASTM D257
Dielectric Strength		V/mil	ASTM D149
Flammability	Nominal Value	Unit	Test Method
Flame Rating - UL			UL 94
Additional Information
Elongation at Break, ASTM D638: 2 to 3% Elongation at Break, ISO 527: 2 to 3% Melt Mass-Flow Rate, ASTM D1238, 300°C/1.2 kg: 5 to 7 g/10 min Melt Mass-Flow Rate, ISO 1133, 300°C/1.2 kg: 5 to 7 g/10 min Notched Izod Impact, ASTM D256: 12 kJ/m²
Related Terminology
Product names can be difficult to match. You may have searched any one of these terms to find this product: DUCTEL® C9704, DUCTEL C9704, DUCTEL® , DUCTEL, DUCTELC9704, C 9704, C9704, Polycarbonate, PC, 9704C

Notes

¹Typical properties: these are not to be construed as specifications.

DUCTEL® C9704