DUCTEL A705(H) Nanjing Lihan Chemical Co., Ltd. Polyamide 66 (Glass Fiber Reinforcement, 25%)

General
Material Status	Commercial: Active
Availability	Asia Pacific
Filler / Reinforcement	Glass Fiber Reinforcement, 25% Filler by Weight
Uses	Bearings
Forms	Pellets

Physical	Dry	Conditioned	Unit	Test Method
Specific Gravity
--		--		ASTM D792
--		--	g/cm³	ISO 1183
Molding Shrinkage - Flow		--	in/in	ASTM D955
Water Absorption
24 hr		--	%	ASTM D570
73°F, 24 hr		--	%	ISO 62
Equilibrium		--	%	ASTM D570
Equilibrium, 73°F, 50% RH		--	%	ISO 62
Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Strength (Break)			psi	ASTM D638, ISO 527-2
Tensile Elongation (Break)			%	ASTM D638, ISO 527-2
Flexural Modulus			psi	ASTM D790, ISO 178
Flexural Strength
--			psi	ISO 178
Yield			psi	ASTM D790
Impact	Dry	Conditioned	Unit	Test Method
Notched Izod Impact Strength			ft·lb/in²	ISO 180
Hardness	Dry	Conditioned	Unit	Test Method
Rockwell Hardness (R-Scale)				ISO 2039-2
Thermal	Dry	Conditioned	Unit	Test Method
Deflection Temperature Under Load
66 psi, Unannealed		--	°F	ASTM D648, ISO 75-2/B
264 psi, Unannealed		--	°F	ASTM D648, ISO 75-2/A
Melting Temperature		--	°F
Electrical	Dry	Conditioned	Unit	Test Method
Surface Resistivity			ohms	ASTM D257
Dielectric Strength		--	V/mil	ASTM D149
Additional Information
Dry	Notched Izod Impact, ASTM D256: 9.5 kJ/m²
Conditioned	Notched Izod Impact, ASTM D256: 14 kJ/m²
Related Terminology
Dry	Product names can be difficult to match. You may have searched any one of these terms to find this product: DUCTEL® A705, DUCTEL A705, DUCTEL® A705(H), DUCTEL A705H, DUCTEL® , DUCTEL, DUCTELA705H, A 705, A705, A 705 H, A705(H), A705H, 705H, Polyamide 66, Nylon 66, Polyamide, Nylon, pa66, Polyamide66, Nylon66, 705A
Generic Name
Dry	Generic Name may also be described by the following terms: PA66.
Conditioned	Product names can be difficult to match. You may have searched any one of these terms to find this product: DUCTEL® A705, DUCTEL A705, DUCTEL® A705(H), DUCTEL A705H, DUCTEL® , DUCTEL, DUCTELA705H, A 705, A705, A 705 H, A705(H), A705H, 705H, Polyamide 66, Nylon 66, Polyamide, Nylon, pa66, Polyamide66, Nylon66, 705A Generic Name may also be described by the following terms: PA66.

Injection	Dry	Unit
Drying Temperature		°F
Drying Time		hr
Processing (Melt) Temp		°F
Mold Temperature		°F

Notes

¹Typical properties: these are not to be construed as specifications.

DUCTEL® A705(H)

Polyamide 66

Glass Fiber Reinforcement, 25%

Supplied by Nanjing Lihan Chemical Co., Ltd.