Specific Gravity
|
|
|
ASTM D792 |
|
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)
|
|
g/10 min
|
ASTM D1238 |
|
Molding Shrinkage - Flow
|
|
in/in
|
ASTM D955 |
|
Water Absorption (73°F, 24 hr)
|
|
%
|
ASTM D570 |
|
Tensile Strength (Ultimate)
|
|
psi
|
ASTM D638 |
|
Flexural Modulus
|
|
psi
|
ASTM D790 |
|
Flexural Strength
|
|
psi
|
ASTM D790 |
|
Charpy Notched Impact Strength (73°F)
|
|
ft·lb/in²
|
ISO 179 |
|
Charpy Unnotched Impact Strength (73°F)
|
|
ft·lb/in²
|
ISO 179 |
|
Notched Izod Impact
|
|
|
ASTM D256A |
|
-4°F
|
|
ft·lb/in
|
|
|
73°F
|
|
ft·lb/in
|
|
|
Rockwell Hardness (R-Scale)
|
|
|
ASTM D785 |
|
Deflection Temperature Under Load (264 psi, Unannealed)
|
|
°F
|
ASTM D648 |
|
Vicat Softening Temperature
|
|
°F
|
ASTM D1525 2 |
|
CLTE - Flow
|
|
in/in/°F
|
ASTM D696 |
|
Surface Resistivity
|
|
ohms
|
ASTM D257 |
|
Dielectric Constant (1 kHz)
|
|
|
ASTM D150 |
|
Comparative Tracking Index
|
|
V
|
IEC 60112 |
|
Flame Rating - UL
|
|
|
UL 94 |
|
0.0630 in
|
|
|
|
|
0.126 in
|
|
|
|
|
The value listed as Charpy Notched Impact Strength, ISO 179, was tested in accordance with DIN 53453.
The value listed as Charpy Unnotched Impact Strength, ISO 179, was tested in accordance with DIN 53453.
The value listed as Comp Track Index, IEC 60112, was tested in accordance with DIN 53480.
CLTE, ASTM D696: 5e-5 to 6e-5 cm/cm/°C
CTI, DIN 53480: >650 V
Fluidity, 250°C, 3 mm: 65 cm
|
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: TECNOPRENE® FK7, TECNOPRENE FK7, TECNOPRENE® , TECNOPRENE, TECNOPRENEFK7, FK 7, FK7, Polypropylene, Unspecified, Polypropylene Unspecified, PP, Unspecified, PP Unspecified, Polypropylene, PP, PolypropyleneUnspecified, PPUnspecified, 7FK
|
|
Generic Name may also be described by the following terms: Polypropilene, Polypropelene.
|