The value listed as Glass Transition Temperature, ASTM E1356, was tested in accordance with ASTM E1545.
Viscosity, 30°C: 260 cps
Density (liquid), 25°C: 1.12 g/cm³
Optical Properties at 355 nm:
- Dp (slope of cure-depth vs. ln(E) curve): 0.16 mm
- Ec (critical exposure): 11.5 mJ/cm²
- E10 (exposure that gives 0.254 mm (0.010 in) thickness): 54 mJ/cm²
Tensile Strength, ASTM D638: 47.1 to 53.6 MPa
Elongation at Break, ASTM D638: 11 to 20%
Elongation at Yield, ASTM D638: 3.3 to 3.5%
Tensile Modulus, ASTM D638: 2650 to 2880 MPa
Flexural Strength, ASTM D790: 63.1 to 74.16 MPa
Flexural Modulus, ASTM D790: 2040 to 2370 MPa
Notched Izod Impact, ASTM D256, Method A: 0.2 to 0.3 J/m
Dielectric Constant, ASTM D150, 60 Hz: 3.9 to 4.1
Dielectric Constant, ASTM D150, 1 kHz: 3.7 to 3.9
Dielectric Constant, ASTM D150, 1 MHz: 3.4 to 3.5
Dielectric Strength, ASTM D149: 15.4 to 16.3 kV/mm
Glass Transition Temperature, ASTM E1545: 39 to 46°C
HDT at 66 psi, ASTM D648: 45.9 to 54.5°C
HDT at 264 psi, ASTM D648: 49.0 to 49.7°C
Tear Strength (Graves), ASTM D1004: 150288 N/m