| Product Description | ||||
|
This data represents typical values that have been calculated from all products classified as: Generic ABS
This information is provided for comparative purposes only. |
||||
| General | ||||
|
Material Status
|
|
|||
|
Availability
|
|
|||
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Specific Gravity
|
|||
|
--
|
1.04 to 1.11
|
|
ASTM D792 |
|
73°F
|
1.03 to 1.06
|
g/cm³
|
ISO 1183 |
|
--
|
0.0377
|
lb/in³
|
ISO 1183 2 |
|
--
|
1.04 to 1.05
|
g/cm³
|
ASTM D1505 |
|
Apparent Density
|
|||
|
--
|
0.60 to 0.61
|
g/cm³
|
ASTM D1895 |
|
--
|
0.60 to 0.65
|
g/cm³
|
ISO 60 |
|
Melt Mass-Flow Rate (MFR)
|
|||
|
220°C/10.0 kg
|
0.60 to 35
|
g/10 min
|
ASTM D1238 |
|
220°C/10.0 kg
|
0.49 to 38
|
g/10 min
|
ISO 1133 |
|
Melt Volume-Flow Rate (MVR)
|
|||
|
--
|
0.0578 to 0.316
|
in³/10min
|
ASTM D1238 |
|
220°C/10.0 kg
|
0.0610 to 2.23
|
in³/10min
|
ISO 1133 |
|
--
|
1.42
|
in³/10min
|
ISO 1133 2 |
|
Molding Shrinkage
|
|||
|
Flow: 73°F
|
0.0045 to 0.0074
|
in/in
|
ASTM D955 |
|
Across Flow: 73°F
|
0.0050 to 0.0090
|
in/in
|
ASTM D955 |
|
73°F
|
0.49 to 0.71
|
%
|
ISO 294-4 |
|
Water Absorption
|
|||
|
73°F, 24 hr
|
0.20 to 0.37
|
%
|
ASTM D570 |
|
73°F, 24 hr
|
0.28 to 0.31
|
%
|
ISO 62 |
|
Saturation, 73°F
|
0.30 to 1.0
|
%
|
ASTM D570 |
|
Saturation, 73°F
|
0.99 to 1.6
|
%
|
ISO 62 |
|
Saturation
|
0.23
|
%
|
ISO 62 2 |
|
Equilibrium, 73°F, 50% RH
|
0.19 to 0.42
|
%
|
ISO 62 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus
|
|||
|
73°F
|
246000 to 410000
|
psi
|
ASTM D638 |
|
73°F
|
279000 to 392000
|
psi
|
ISO 527-2 |
|
--
|
318000
|
psi
|
ISO 527-2 2 |
|
Tensile Strength
|
|||
|
Yield, 73°F
|
5240 to 7620
|
psi
|
ASTM D638 |
|
Yield, 73°F
|
5200 to 7620
|
psi
|
ISO 527-2 |
|
Yield
|
6110
|
psi
|
ISO 527-2 2 |
|
Break, 73°F
|
3830 to 6180
|
psi
|
ASTM D638 |
|
Break, 73°F
|
3980 to 5810
|
psi
|
ISO 527-2 |
|
73°F
|
4660 to 7750
|
psi
|
ASTM D638 |
|
Tensile Elongation
|
|||
|
Yield, 73°F
|
2.0 to 12
|
%
|
ASTM D638 |
|
Yield, 73°F
|
1.5 to 3.2
|
%
|
ISO 527-2 |
|
Yield
|
5.5
|
%
|
ISO 527-2 2 |
|
Break, 73°F
|
1.0 to 57
|
%
|
ASTM D638 |
|
Break, 73°F
|
3.4 to 36
|
%
|
ISO 527-2 |
|
Nominal Tensile Strain at Break
|
|||
|
73°F
|
8.8 to 12
|
%
|
ISO 527-2 |
|
--
|
9.0 to 50
|
%
|
ISO 527-2 2 |
|
Flexural Modulus
|
|||
|
73°F
|
205000 to 400000
|
psi
|
ASTM D790 |
|
73°F
|
233000 to 385000
|
psi
|
ISO 178 |
|
Flexural Strength
|
|||
|
73°F
|
6320 to 12600
|
psi
|
ASTM D790 |
|
73°F
|
7610 to 13400
|
psi
|
ISO 178 |
|
Yield, 73°F
|
7940 to 11700
|
psi
|
ASTM D790 |
|
Break, 73°F
|
7730 to 11000
|
psi
|
ASTM D790 |
|
Coefficient of Friction
|
0.11 to 0.46
|
|
ASTM D1894 |
|
Taber Abrasion Resistance (73°F)
|
69.0 to 117
|
mg
|
ASTM D1044 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
|||
|
73°F
|
2.7 to 14
|
ft·lb/in²
|
ISO 179 |
|
-22°F
|
5.17
|
ft·lb/in²
|
ISO 179/1eA 2 |
|
73°F
|
15.6
|
ft·lb/in²
|
ISO 179/1eA 2 |
|
Charpy Unnotched Impact Strength
|
|||
|
73°F
|
3.8 to 89
|
ft·lb/in²
|
ISO 179 |
|
-22°F
|
25.4
|
ft·lb/in²
|
ISO 179/1eU 2 |
|
Notched Izod Impact
|
|||
|
73°F
|
1.3 to 8.6
|
ft·lb/in
|
ASTM D256 |
|
73°F
|
1.1 to 14
|
ft·lb/in²
|
ISO 180 |
|
Unnotched Izod Impact
|
|||
|
73°F
|
1.7 to 32
|
ft·lb/in
|
ASTM D256 |
|
73°F
|
3.4 to 48
|
ft·lb/in²
|
ISO 180 |
|
Instrumented Dart Impact
|
|||
|
73°F
|
176 to 409
|
in·lb
|
ASTM D3763 |
|
73°F
|
2.73 to 7.55
|
ft·lb
|
ISO 6603-2 |
|
Gardner Impact (73°F)
|
110 to 317
|
in·lb
|
ASTM D3029 |
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Rockwell Hardness
|
|||
|
73°F
|
94 to 116
|
|
ASTM D785 |
|
73°F
|
101 to 116
|
|
ISO 2039-2 |
|
Durometer Hardness (73°F)
|
40 to 94
|
|
ASTM D2240 |
|
Ball Indentation Hardness
|
10800 to 16800
|
psi
|
ISO 2039-1 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load
|
|||
|
66 psi, Unannealed
|
179 to 224
|
°F
|
ASTM D648 |
|
66 psi, Unannealed
|
161 to 222
|
°F
|
ISO 75-2/B |
|
66 psi, Annealed
|
210 to 220
|
°F
|
ASTM D648 |
|
264 psi, Unannealed
|
165 to 198
|
°F
|
ASTM D648 |
|
264 psi, Unannealed
|
164 to 206
|
°F
|
ISO 75-2/A |
|
264 psi, Annealed
|
185 to 248
|
°F
|
ASTM D648 |
|
264 psi, Annealed
|
184 to 220
|
°F
|
ISO 75-2/A |
|
264 psi
|
193
|
°F
|
ISO 75-2 2 |
|
Max. Continuous Use Temperature
|
140 to 176
|
°F
|
ASTM D794 |
|
Glass Transition Temperature 3
|
220
|
°F
|
ISO 11357-2 2 |
|
Vicat Softening Temperature
|
|||
|
--
|
192 to 226
|
°F
|
ASTM D1525 |
|
--
|
190 to 231
|
°F
|
ISO 306 |
|
50°C/h, B (50N)
|
206
|
°F
|
ISO 306 2 |
|
Ball Indentation Temperature
|
167 to 195
|
°F
|
IEC 60598-1 |
|
Ball Pressure Test
|
Pass
|
|
IEC 60695-10-2 |
|
CLTE
|
|||
|
Flow
|
0.000047 to 0.000050
|
in/in/°F
|
ASTM D696 |
|
Flow
|
0.000044 to 0.000057
|
in/in/°F
|
ASTM E831 |
|
Flow
|
0.000044 to 0.000053
|
in/in/°F
|
ISO 11359-2 |
|
Flow
|
0.000051
|
in/in/°F
|
ISO 11359-2 2 |
|
Transverse
|
0.000047 to 0.000062
|
in/in/°F
|
ASTM E831 |
|
Transverse
|
0.000044 to 0.000053
|
in/in/°F
|
ISO 11359-2 |
|
Transverse
|
0.000049
|
in/in/°F
|
ISO 11359-2 2 |
|
Thermal Conductivity
|
|||
|
73°F
|
1.0 to 1.5
|
Btu·in/hr/ft²/°F
|
ASTM C177 |
|
73°F
|
1.2 to 1.4
|
Btu·in/hr/ft²/°F
|
ISO 8302 |
| Electrical |
Nominal Value
|
Unit
|
Test Method
|
|
Surface Resistivity
|
|||
|
--
|
0.51 to 1.0E+15
|
ohm
|
ASTM D257 |
|
--
|
1.0E+4 to 5.0E+15
|
ohm
|
IEC 60093 |
|
--
|
9.8E+14 to 1.0E+15
|
ohm
|
IEC 60093 2 |
|
Volume Resistivity
|
|||
|
73°F
|
0.15 to 1.3E+16
|
ohm·cm
|
ASTM D257 |
|
73°F
|
1.0E+13 to 2.5E+16
|
ohm·cm
|
IEC 60093 |
|
--
|
3.8E+14 to 3.9E+14
|
ohm·in
|
IEC 60093 2 |
|
Dielectric Strength
|
|||
|
73°F
|
390 to 890
|
V/mil
|
ASTM D149 |
|
73°F
|
340 to 2200
|
V/mil
|
IEC 60243-1 |
|
--
|
1200
|
V/mil
|
IEC 60243-1 2 |
|
Dielectric Constant
|
|||
|
73°F
|
2.80 to 3.36
|
|
ASTM D150 |
|
73°F
|
2.90 to 3.20
|
|
IEC 60250 |
|
73°F
|
2.75
|
|
IEC 60250 |
|
1 MHz
|
2.81
|
|
IEC 60250 2 |
|
Dissipation Factor
|
|||
|
73°F
|
0.0040 to 0.015
|
|
ASTM D150, IEC 60250 |
|
1 MHz
|
0.011
|
|
IEC 60250 2 |
|
Arc Resistance
|
5.00 to 7.43
|
sec
|
ASTM D495 |
|
Comparative Tracking Index
|
585 to 600
|
V
|
IEC 60112 |
| Flammability |
Nominal Value
|
Unit
|
Test Method
|
|
Burning Rate
|
0.90 to 2.7
|
in/min
|
ISO 3795 |
|
Glow Wire Flammability Index
|
1190 to 1760
|
°F
|
IEC 60695-2-12 |
|
Glow Wire Ignition Temperature
|
1020 to 1760
|
°F
|
IEC 60695-2-13 |
|
Oxygen Index
|
21 to 28
|
%
|
ASTM D2863 |
| UL |
Nominal Value
|
Unit
|
Test Method
|
|
RTI Str
|
138 to 140
|
°F
|
UL 746 |
|
RTI Imp
|
138 to 140
|
°F
|
UL 746 |
|
RTI Elec
|
138 to 140
|
°F
|
UL 746 |
|
High Voltage Arc Tracking Rate (HVTR)
|
0.00 to 0.147
|
in/min
|
UL 746 |
|
Hot-wire Ignition (HWI)
|
14 to 34
|
sec
|
UL 746 |
|
High Amp Arc Ignition (HAI)
|
195 to 200
|
|
UL 746 |
| Optical |
Nominal Value
|
Unit
|
Test Method
|
|
Gardner Gloss
|
24 to 125
|
|
ASTM D523 |
|
Gloss
|
30 to 98
|
|
ASTM D2457 |
|
Gloss
|
89 to 90
|
|
ISO 2813 |
|
Transmittance
|
85.8 to 91.6
|
%
|
ASTM D1003 |
|
Haze
|
1.3 to 4.3
|
%
|
ASTM D1003 |
|
Yellowness Index
|
0.50 to 32
|
YI
|
ASTM D1925 |
| Injection |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
165 to 191
|
°F
|
|
|
Drying Time
|
2.0 to 3.6
|
hr
|
|
|
Drying Time, Maximum
|
7.5
|
hr
|
|
|
Dew Point
|
-0.500 to 0.00
|
°F
|
|
|
Suggested Max Moisture
|
0.010 to 0.11
|
%
|
|
|
Suggested Shot Size
|
60 to 63
|
%
|
|
|
Suggested Max Regrind
|
13
|
%
|
|
|
Hopper Temperature
|
158 to 473
|
°F
|
|
|
Rear Temperature
|
350 to 475
|
°F
|
|
|
Middle Temperature
|
372 to 466
|
°F
|
|
|
Front Temperature
|
381 to 474
|
°F
|
|
|
Nozzle Temperature
|
406 to 477
|
°F
|
|
|
Processing (Melt) Temp
|
407 to 501
|
°F
|
|
|
Melt Temperature (Aim)
|
452
|
°F
|
|
|
Mold Temperature
|
120 to 161
|
°F
|
|
|
Injection Pressure
|
521 to 15300
|
psi
|
|
|
Holding Pressure
|
498 to 7670
|
psi
|
|
|
Back Pressure
|
0.725 to 285
|
psi
|
|
|
Screw Speed
|
45 to 77
|
rpm
|
|
|
Clamp Tonnage
|
3.3
|
tons/in²
|
|
|
Cushion
|
0.125 to 0.375
|
in
|
|
|
Vent Depth
|
0.0018
|
in
|
|
| Injection Notes | |||
|
This data represents typical values that have been calculated from all products classified as: Generic ABS
This information is provided for comparative purposes only. |
|||
| Extrusion |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
167 to 195
|
°F
|
|
|
Drying Time
|
2.0 to 3.7
|
hr
|
|
|
Suggested Max Moisture
|
0.0085 to 0.053
|
%
|
|
|
Cylinder Zone 1 Temp.
|
329 to 494
|
°F
|
|
|
Cylinder Zone 2 Temp.
|
368 to 447
|
°F
|
|
|
Cylinder Zone 3 Temp.
|
378 to 458
|
°F
|
|
|
Cylinder Zone 4 Temp.
|
385 to 447
|
°F
|
|
|
Cylinder Zone 5 Temp.
|
392 to 446
|
°F
|
|
|
Adapter Temperature
|
418 to 449
|
°F
|
|
|
Melt Temperature
|
385 to 475
|
°F
|
|
|
Die Temperature
|
390 to 455
|
°F
|
|
|
Take-Off Roll
|
182 to 194
|
°F
|
|
| Extrusion Notes | |||
|
This data represents typical values that have been calculated from all products classified as: Generic ABS
This information is provided for comparative purposes only. |
|||
| Notes |
| 1Typical properties: these are not to be construed as specifications. |
| 2Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 318 °F/min |