| Product Description | ||||
|
This data represents typical values that have been calculated from all products classified as: Generic Epoxy
This information is provided for comparative purposes only. |
||||
| General | ||||
|
Material Status
|
|
|||
|
Availability
|
|
|||
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Specific Gravity
|
|||
|
--
|
1.01 to 2.00
|
|
ASTM D792 |
|
73°F
|
0.994 to 1.43
|
g/cm³
|
ISO 1183 |
|
--
|
0.650 to 1.77
|
g/cm³
|
ASTM D1505 |
|
Apparent Density
|
1.02 to 1.61
|
g/cm³
|
ASTM D1895 |
|
Molding Shrinkage - Flow (73°F)
|
0.00010 to 0.0051
|
in/in
|
ASTM D955 |
|
Water Absorption
|
ASTM D570 | ||
|
73°F, 24 hr
|
0.060 to 0.41
|
%
|
|
|
Saturation, 73°F
|
0.20 to 0.87
|
%
|
|
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus (73°F)
|
27000 to 2.67E+6
|
psi
|
ASTM D638 |
|
Tensile Strength
|
|||
|
Yield, 73°F
|
464 to 26100
|
psi
|
ASTM D638 |
|
Yield, 73°F
|
4350 to 11000
|
psi
|
ISO 527-2 |
|
Break, 73°F
|
1950 to 35800
|
psi
|
ASTM D638 |
|
Ultimate, 73°F
|
520 to 8270
|
psi
|
ASTM D638 |
|
73°F
|
0.900 to 8930
|
psi
|
ASTM D638 |
|
Tensile Elongation
|
ASTM D638 | ||
|
Yield, 73°F
|
0.40 to 7.9
|
%
|
|
|
Break, 73°F
|
0.63 to 21
|
%
|
|
|
Flexural Modulus (73°F)
|
170 to 1.80E+6
|
psi
|
ASTM D790 |
|
Flexural Strength
|
|||
|
73°F
|
0.996 to 27300
|
psi
|
ASTM D790 |
|
73°F
|
12300 to 14500
|
psi
|
ISO 178 |
|
Yield, 73°F
|
120 to 36100
|
psi
|
ASTM D790 |
|
Break, 73°F
|
8290 to 31000
|
psi
|
ASTM D790 |
|
Compressive Modulus
|
3430 to 419000
|
psi
|
ASTM D695 |
|
Compressive Strength (73°F)
|
3360 to 25200
|
psi
|
ASTM D695 |
|
Shear Strength (73°F)
|
988 to 7750
|
psi
|
ASTM D732 |
| Elastomers |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Strength (Break, 73°F)
|
2490 to 8200
|
psi
|
ASTM D412 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Notched Izod Impact (73°F)
|
0.20 to 1.2
|
ft·lb/in
|
ASTM D256 |
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Durometer Hardness
|
|||
|
73°F
|
69 to 93
|
|
ASTM D2240 |
|
73°F
|
79 to 88
|
|
ISO 868 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load
|
ASTM D648 | ||
|
66 psi, Unannealed
|
120 to 470
|
°F
|
|
|
264 psi, Unannealed
|
75.0 to 480
|
°F
|
|
|
Max. Continuous Use Temperature
|
158 to 356
|
°F
|
ASTM D794 |
|
Glass Transition Temperature
|
|||
|
--
|
271 to 442
|
°F
|
ASTM E1356 |
|
--
|
125 to 340
|
°F
|
DSC |
|
CLTE - Flow
|
3.2E-6 to 0.000065
|
in/in/°F
|
ASTM D696 |
|
Thermal Conductivity
|
|||
|
73°F
|
0.43 to 6.0
|
Btu·in/hr/ft²/°F
|
ASTM C177 |
|
73°F
|
1.4 to 2.9
|
Btu·in/hr/ft²/°F
|
ISO 8302 |
| Electrical |
Nominal Value
|
Unit
|
Test Method
|
|
Surface Resistivity
|
4.0E+10 to 1.5E+16
|
ohm
|
ASTM D257 |
|
Volume Resistivity
|
|||
|
73°F
|
0.00015 to 5.0E+16
|
ohm·cm
|
ASTM D257 |
|
73°F
|
0.00050 to 2.5E+15
|
ohm·cm
|
IEC 60093 |
|
Dielectric Strength
|
|||
|
73°F
|
56 to 920
|
V/mil
|
ASTM D149 |
|
73°F
|
410 to 640
|
V/mil
|
IEC 60243-1 |
|
Dielectric Constant (73°F)
|
3.16 to 5.29
|
|
ASTM D150 |
|
Dissipation Factor (73°F)
|
0.0010 to 0.031
|
|
ASTM D150 |
|
Arc Resistance
|
177 to 180
|
sec
|
ASTM D495 |
| Flammability |
Nominal Value
|
Unit
|
Test Method
|
|
Oxygen Index
|
30 to 34
|
%
|
ASTM D2863 |
| Optical |
Nominal Value
|
Unit
|
Test Method
|
|
Refractive Index
|
1.508 to 1.546
|
|
ASTM D542 |
|
Transmittance
|
86.8 to 99.0
|
%
|
ASTM D1003 |
| Thermoset |
Nominal Value
|
Unit
|
Test Method
|
|
Pot Life (73°F)
|
1.0 to 6500
|
min
|
|
|
Shelf Life (73°F)
|
24 to 54
|
wk
|
|
|
Thermoset Mix Viscosity (73°F)
|
150 to 23600
|
cP
|
ASTM D2393 |
|
Demold Time (73°F)
|
4.5 to 10000
|
min
|
|
| Fill Analysis |
Nominal Value
|
Unit
|
Test Method
|
|
Melt Viscosity (73.0°F)
|
0.550 to 0.974
|
Pa·s
|
ASTM D3835 |
| Notes |
| 1Typical properties: these are not to be construed as specifications. |