| Product Description | ||||
|
This data represents typical values that have been calculated from all products classified as: Generic HDPE
This information is provided for comparative purposes only. |
||||
| General | ||||
|
Material Status
|
|
|||
|
Availability
|
|
|||
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Specific Gravity
|
|||
|
--
|
0.936 to 0.966
|
|
ASTM D792 |
|
73°F
|
0.940 to 0.972
|
g/cm³
|
ISO 1183 |
|
--
|
0.0336
|
lb/in³
|
ISO 1183 2 |
|
--
|
0.941 to 0.963
|
g/cm³
|
ASTM D1505 |
|
--
|
0.944 to 0.963
|
g/cm³
|
ASTM D4883 |
|
Apparent Density
|
|||
|
--
|
0.33 to 0.61
|
g/cm³
|
ASTM D1895 |
|
--
|
0.46 to 0.55
|
g/cm³
|
ISO 60 |
|
Melt Mass-Flow Rate (MFR)
|
|||
|
190°C/2.16 kg
|
0.020 to 7.5
|
g/10 min
|
ASTM D1238 |
|
190°C/2.16 kg
|
0.030 to 10
|
g/10 min
|
ISO 1133 |
|
Melt Volume-Flow Rate (MVR)
|
|||
|
190°C/5.0 kg
|
0.999 to 2.26
|
in³/10min
|
ISO 1133 |
|
--
|
0.0394
|
in³/10min
|
ISO 1133 2 |
|
Molding Shrinkage
|
|||
|
Flow: 73°F
|
0.00018 to 0.030
|
in/in
|
ASTM D955 |
|
Across Flow: 73°F
|
0.0096 to 0.025
|
in/in
|
ASTM D955 |
|
73°F
|
1.5 to 2.0
|
%
|
ISO 294-4 |
|
Water Absorption (73°F, 24 hr)
|
0.010 to 0.017
|
%
|
ASTM D570 |
|
Environmental Stress-Cracking Resistance (73°F)
|
0.500 to 1130
|
hr
|
ASTM D1693 |
|
Viscosity Number (Reduced Viscosity) (73°F)
|
130.0 to 400.3
|
ml/g
|
ISO 1628 |
|
Carbon Black Content
|
1.0 to 2.6
|
%
|
ASTM D1603 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus
|
|||
|
73°F
|
30800 to 184000
|
psi
|
ASTM D638 |
|
73°F
|
120000 to 190000
|
psi
|
ISO 527-2 |
|
--
|
161000
|
psi
|
ISO 527-2 2 |
|
Tensile Strength
|
|||
|
Yield, 73°F
|
2450 to 4600
|
psi
|
ASTM D638 |
|
Yield, 73°F
|
3160 to 4520
|
psi
|
ISO 527-2 |
|
Yield
|
3640
|
psi
|
ISO 527-2 2 |
|
Break, 73°F
|
1890 to 5730
|
psi
|
ASTM D638 |
|
Break, 73°F
|
1840 to 5890
|
psi
|
ISO 527-2 |
|
Ultimate, 73°F
|
3420 to 4850
|
psi
|
ASTM D638 |
|
73°F
|
2680 to 3710
|
psi
|
ASTM D638 |
|
Tensile Elongation
|
|||
|
Yield, 73°F
|
1.0 to 22
|
%
|
ASTM D638 |
|
Yield, 73°F
|
5.0 to 20
|
%
|
ISO 527-2 |
|
Yield
|
11
|
%
|
ISO 527-2 2 |
|
Break, 73°F
|
1.0 to 1100
|
%
|
ASTM D638 |
|
Break, 73°F
|
6.0 to 1000
|
%
|
ISO 527-2 |
|
Tensile Creep Modulus
|
ISO 899-1 | ||
|
1 hr
|
91700
|
psi
|
|
|
1000 hr
|
42400
|
psi
|
|
|
Apparent Bending Modulus
|
86600 to 171000
|
psi
|
ASTM D747 |
|
Flexural Modulus
|
|||
|
73°F
|
100000 to 250000
|
psi
|
ASTM D790 |
|
73°F
|
119000 to 234000
|
psi
|
ISO 178 |
|
Flexural Strength
|
|||
|
73°F
|
2650 to 6100
|
psi
|
ASTM D790 |
|
73°F
|
2730 to 3420
|
psi
|
ISO 178 |
|
Yield, 73°F
|
3790 to 4630
|
psi
|
ASTM D790 |
|
Coefficient of Friction
|
0.20 to 0.30
|
|
ASTM D1894 |
| Films |
Nominal Value
|
Unit
|
Test Method
|
|
Film Thickness - Tested
|
0.39 to 1.9
|
mil
|
|
|
Film Puncture Force
|
6.70 to 48.7
|
lbf
|
|
|
Secant Modulus
|
|||
|
MD
|
39700 to 185000
|
psi
|
ASTM D882 |
|
TD
|
88900 to 217000
|
psi
|
ASTM D882 |
|
73°F
|
58000 to 120000
|
psi
|
ISO 527-3 |
|
Tensile Strength
|
|||
|
MD: Yield
|
2950 to 5170
|
psi
|
ASTM D882 |
|
TD: Yield
|
3100 to 4710
|
psi
|
ASTM D882 |
|
Yield, 73°F
|
3120 to 6560
|
psi
|
ISO 527-3 |
|
MD: Break
|
3310 to 14500
|
psi
|
ASTM D882 |
|
TD: Break
|
2180 to 8650
|
psi
|
ASTM D882 |
|
Break, 73°F
|
3050 to 9570
|
psi
|
ISO 527-3 |
|
73°F
|
3610 to 9550
|
psi
|
ISO 527-3 |
|
Tensile Elongation
|
|||
|
MD: Break
|
230 to 660
|
%
|
ASTM D882 |
|
TD: Break
|
3.0 to 950
|
%
|
ASTM D882 |
|
Break, 73°F
|
280 to 830
|
%
|
ISO 527-3 |
|
Dart Drop Impact
|
|||
|
73°F
|
7.0 to 260
|
g
|
ASTM D1709 |
|
73°F
|
40 to 350
|
g
|
ISO 7765-1 |
|
Elmendorf Tear Strength
|
|||
|
MD
|
0.40 to 40
|
g
|
ASTM D1922 |
|
TD
|
6.2 to 360
|
g
|
ASTM D1922 |
|
--
|
0.00057 to 0.18
|
lbf
|
ISO 6383-2 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
|||
|
73°F
|
0.57 to 13
|
ft·lb/in²
|
ISO 179 |
|
73°F
|
13.6
|
ft·lb/in²
|
ISO 179/1eA 2 |
|
Charpy Unnotched Impact Strength (73°F)
|
0.95 to 9.9
|
ft·lb/in²
|
ISO 179 |
|
Notched Izod Impact
|
|||
|
73°F
|
0.42 to 9.6
|
ft·lb/in
|
ASTM D256 |
|
73°F
|
0.90 to 15
|
ft·lb/in²
|
ISO 180 |
|
Unnotched Izod Impact (73°F)
|
0.13 to 20
|
ft·lb/in
|
ASTM D256 |
|
Tensile Impact Strength
|
|||
|
73°F
|
18.6 to 134
|
ft·lb/in²
|
ASTM D1822 |
|
73°F
|
29.1
|
ft·lb/in²
|
ISO 8256 |
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Rockwell Hardness (73°F)
|
50 to 61
|
|
ASTM D785 |
|
Durometer Hardness
|
|||
|
73°F
|
60 to 71
|
|
ASTM D2240 |
|
73°F
|
57 to 69
|
|
ISO 868 |
|
Ball Indentation Hardness
|
5800 to 8300
|
psi
|
ISO 2039-1 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load
|
|||
|
66 psi, Unannealed
|
150 to 180
|
°F
|
ASTM D648 |
|
66 psi, Unannealed
|
148 to 202
|
°F
|
ISO 75-2/B |
|
264 psi, Unannealed
|
98.0 to 178
|
°F
|
ASTM D648 |
|
264 psi, Unannealed
|
106 to 120
|
°F
|
ISO 75-2/A |
|
264 psi
|
143
|
°F
|
ISO 75-2 2 |
|
Brittleness Temperature
|
|||
|
--
|
-180 to -75.7
|
°F
|
ASTM D746 |
|
--
|
-94.5 to -75.6
|
°F
|
ISO 974 |
|
Vicat Softening Temperature
|
|||
|
--
|
244 to 274
|
°F
|
ASTM D1525 |
|
--
|
157 to 269
|
°F
|
ISO 306 |
|
50°C/h, B (50N)
|
152
|
°F
|
ISO 306 2 |
|
Melting Temperature
|
|||
|
--
|
263 to 276
|
°F
|
|
|
--
|
264 to 277
|
°F
|
DSC |
|
--
|
259 to 278
|
°F
|
ISO 11357-3 |
|
--
|
259 to 275
|
°F
|
ASTM D3418 |
|
--
|
266 to 275
|
°F
|
ISO 3146 |
|
-- 3
|
294
|
°F
|
ISO 11357-3 2 |
|
Peak Crystallization Temperature (DSC)
|
|||
|
--
|
233 to 274
|
°F
|
ASTM D3418 |
|
--
|
267 to 270
|
°F
|
ISO 3146 |
|
CLTE - Flow
|
0.000075 to 0.00012
|
in/in/°F
|
ASTM D696 |
|
Specific Heat (73°F)
|
0.448 to 0.550
|
Btu/lb/°F
|
ASTM C351 |
|
Thermal Conductivity (73°F)
|
3.3
|
Btu·in/hr/ft²/°F
|
ASTM C177 |
| Electrical |
Nominal Value
|
Unit
|
Test Method
|
|
Surface Resistivity
|
|||
|
--
|
40 to 2.5E+13
|
ohm
|
ASTM D257 |
|
--
|
1.6E+2 to 2.5E+14
|
ohm
|
IEC 60093 |
|
Volume Resistivity
|
|||
|
73°F
|
10 to 2.5E+18
|
ohm·cm
|
ASTM D257 |
|
73°F
|
10 to 1.2E+16
|
ohm·cm
|
IEC 60093 |
|
Dielectric Strength
|
|||
|
73°F
|
500 to 1200
|
V/mil
|
ASTM D149 |
|
73°F
|
430 to 3800
|
V/mil
|
IEC 60243-1 |
|
Dielectric Constant
|
|||
|
73°F
|
2.28 to 2.31
|
|
ASTM D150 |
|
73°F
|
2.32 to 2.56
|
|
ASTM D1531 |
|
73°F
|
2.32 to 2.50
|
|
IEC 60250 |
|
1 MHz
|
2.30
|
|
IEC 60250 2 |
|
Dissipation Factor
|
|||
|
73°F
|
0.000020 to 0.00027
|
|
ASTM D150 |
|
73°F
|
0.000057 to 0.00030
|
|
ASTM D1531 |
|
73°F
|
0.000050 to 0.00042
|
|
IEC 60250 |
|
1 MHz
|
0.00030
|
|
IEC 60250 2 |
| Optical |
Nominal Value
|
Unit
|
Test Method
|
|
Gloss
|
5 to 120
|
|
ASTM D2457 |
|
Haze
|
3.0 to 81
|
%
|
ASTM D1003 |
|
Yellowness Index
|
0.0 to 4.0
|
YI
|
ASTM D1925 |
| Injection |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
175
|
°F
|
|
|
Drying Time
|
2.0 to 3.0
|
hr
|
|
|
Rear Temperature
|
363 to 478
|
°F
|
|
|
Middle Temperature
|
361 to 478
|
°F
|
|
|
Front Temperature
|
437 to 478
|
°F
|
|
|
Nozzle Temperature
|
453 to 476
|
°F
|
|
|
Processing (Melt) Temp
|
356 to 484
|
°F
|
|
|
Mold Temperature
|
57.1 to 110
|
°F
|
|
|
Injection Pressure
|
11100 to 12500
|
psi
|
|
| Injection Notes | |||
|
This data represents typical values that have been calculated from all products classified as: Generic HDPE
This information is provided for comparative purposes only. |
|||
| Extrusion |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
176 to 196
|
°F
|
|
|
Drying Time
|
1.9 to 3.1
|
hr
|
|
|
Cylinder Zone 1 Temp.
|
304 to 483
|
°F
|
|
|
Cylinder Zone 2 Temp.
|
333 to 416
|
°F
|
|
|
Cylinder Zone 3 Temp.
|
356 to 473
|
°F
|
|
|
Cylinder Zone 4 Temp.
|
296 to 478
|
°F
|
|
|
Cylinder Zone 5 Temp.
|
374 to 451
|
°F
|
|
|
Adapter Temperature
|
302 to 478
|
°F
|
|
|
Melt Temperature
|
363 to 420
|
°F
|
|
|
Die Temperature
|
361 to 447
|
°F
|
|
| Extrusion Notes | |||
|
This data represents typical values that have been calculated from all products classified as: Generic HDPE
This information is provided for comparative purposes only. |
|||
| Notes |
| 1Typical properties: these are not to be construed as specifications. |
| 2Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 318 °F/min |