| Product Description | ||||
|
This data represents typical values that have been calculated from all products classified as: Generic PUR, Unspecified
This information is provided for comparative purposes only. |
||||
| General | ||||
|
Material Status
|
|
|||
|
Availability
|
|
|||
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Specific Gravity
|
|||
|
--
|
0.871 to 1.42
|
|
ASTM D792 |
|
73°F
|
0.600 to 7.50
|
g/cm³
|
ISO 1183 |
|
Apparent Density
|
0.94 to 1.51
|
g/cm³
|
ASTM D1895 |
|
Molding Shrinkage
|
|||
|
Flow: 73°F
|
0.00010 to 0.013
|
in/in
|
ASTM D955 |
|
73°F
|
0.30 to 1.2
|
%
|
ISO 294-4 |
|
Water Absorption
|
ASTM D570 | ||
|
73°F, 24 hr
|
0.060 to 0.42
|
%
|
|
|
Saturation, 73°F
|
0.16 to 0.50
|
%
|
|
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus
|
|||
|
73°F
|
700 to 316000
|
psi
|
ASTM D638 |
|
73°F
|
21800 to 290000
|
psi
|
ISO 527-2 |
|
Tensile Strength
|
|||
|
Yield, 73°F
|
11.0 to 6960
|
psi
|
ASTM D638 |
|
Yield, 73°F
|
2310 to 7000
|
psi
|
ISO 527-2 |
|
Break, 73°F
|
2420 to 8310
|
psi
|
ASTM D638 |
|
Break, 73°F
|
1260 to 3700
|
psi
|
ISO 527-2 |
|
73°F
|
1490 to 7610
|
psi
|
ASTM D638 |
|
Tensile Elongation
|
|||
|
Yield, 73°F
|
2.0 to 130
|
%
|
ASTM D638 |
|
Yield, 73°F
|
4.8 to 42
|
%
|
ISO 527-2 |
|
Break, 73°F
|
0.40 to 17
|
%
|
ASTM D638 |
|
Break, 73°F
|
3.0 to 28
|
%
|
ISO 527-2 |
|
Flexural Modulus
|
|||
|
73°F
|
5500 to 368000
|
psi
|
ASTM D790 |
|
73°F
|
57100 to 248000
|
psi
|
ISO 178 |
|
Flexural Strength
|
ASTM D790 | ||
|
73°F
|
290 to 11800
|
psi
|
|
|
Yield, 73°F
|
750 to 15600
|
psi
|
|
|
Compressive Modulus
|
32200 to 360000
|
psi
|
ASTM D695 |
|
Compressive Strength (73°F)
|
30.0 to 10400
|
psi
|
ASTM D695 |
| Elastomers |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Stress
|
ASTM D412 | ||
|
100% Strain, 73°F
|
25.0 to 846
|
psi
|
|
|
200% Strain, 73°F
|
200 to 308
|
psi
|
|
|
300% Strain, 73°F
|
285 to 1460
|
psi
|
|
|
Tensile Strength
|
ASTM D412 | ||
|
Yield, 73°F
|
300 to 9570
|
psi
|
|
|
Break, 73°F
|
200 to 920
|
psi
|
|
|
Tensile Elongation
|
ASTM D412 | ||
|
Yield
|
320 to 800
|
%
|
|
|
Break, 73°F
|
2.0 to 1000
|
%
|
|
|
Tear Strength (73°F)
|
12.2 to 331
|
lbf/in
|
ASTM D624 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Notched Izod Impact (73°F)
|
0.18 to 1.8
|
ft·lb/in
|
ASTM D256 |
|
Unnotched Izod Impact (73°F)
|
0.44 to 30
|
ft·lb/in
|
ASTM D256 |
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Durometer Hardness
|
|||
|
73°F
|
49 to 90
|
|
ASTM D2240 |
|
73°F
|
29 to 92
|
|
ISO 868 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load
|
|||
|
66 psi, Unannealed
|
126 to 225
|
°F
|
ASTM D648 |
|
66 psi, Unannealed
|
133 to 172
|
°F
|
ISO 75-2/B |
|
264 psi, Unannealed
|
102 to 195
|
°F
|
ASTM D648 |
|
264 psi, Unannealed
|
95.0 to 249
|
°F
|
ISO 75-2/A |
|
Max. Continuous Use Temperature
|
263 to 266
|
°F
|
ASTM D794 |
|
Glass Transition Temperature
|
140 to 221
|
°F
|
ASTM E1356 |
|
Ball Pressure Test
|
Pass
|
|
IEC 60695-10-2 |
|
CLTE
|
|||
|
Flow
|
0.000054 to 0.00010
|
in/in/°F
|
ASTM D696 |
|
Flow
|
0.000040 to 0.000067
|
in/in/°F
|
ISO 11359-2 |
|
Transverse
|
0.000040 to 0.000074
|
in/in/°F
|
ISO 11359-2 |
|
Thermal Conductivity
|
|||
|
73°F
|
0.26 to 2.3
|
Btu·in/hr/ft²/°F
|
ASTM C177 |
|
73°F
|
0.62 to 1.8
|
Btu·in/hr/ft²/°F
|
ISO 8302 |
| Electrical |
Nominal Value
|
Unit
|
Test Method
|
|
Surface Resistivity
|
4.0 to 1.7E+16
|
ohm
|
ASTM D257 |
|
Volume Resistivity
|
|||
|
73°F
|
5.2E+6 to 3.0E+15
|
ohm·cm
|
ASTM D257 |
|
73°F
|
3.8E+9 to 7.4E+14
|
ohm·cm
|
IEC 60093 |
|
Dielectric Strength
|
|||
|
73°F
|
460 to 720
|
V/mil
|
ASTM D149 |
|
73°F
|
480 to 910
|
V/mil
|
IEC 60243-1 |
|
Dielectric Constant (73°F)
|
2.69 to 5.82
|
|
ASTM D150 |
|
Dissipation Factor (73°F)
|
0.00030 to 0.045
|
|
ASTM D150 |
|
Arc Resistance
|
120 to 122
|
sec
|
ASTM D495 |
| Thermoset |
Nominal Value
|
Unit
|
Test Method
|
|
Pot Life (73°F)
|
0.033 to 41
|
min
|
|
|
Shelf Life (73°F)
|
24 to 78
|
wk
|
|
|
Thermoset Mix Viscosity (73°F)
|
35.0 to 15000
|
cP
|
ASTM D2393 |
|
Demold Time (73°F)
|
4.5 to 10000
|
min
|
|
|
Post Cure Time (73°F)
|
140 to 180
|
hr
|
|
| Fill Analysis |
Nominal Value
|
Unit
|
Test Method
|
|
Melt Viscosity (73.0°F)
|
470 to 3300
|
mPa·s
|
ASTM D3236 |
|
Melt Viscosity (73.0°F)
|
0.0700 to 104
|
Pa·s
|
ASTM D3835 |
| Injection |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
177 to 225
|
°F
|
|
|
Drying Time
|
2.9 to 5.0
|
hr
|
|
|
Suggested Max Moisture
|
0.010 to 0.030
|
%
|
|
|
Rear Temperature
|
370 to 371
|
°F
|
|
|
Middle Temperature
|
380 to 381
|
°F
|
|
|
Front Temperature
|
390 to 391
|
°F
|
|
|
Processing (Melt) Temp
|
398 to 450
|
°F
|
|
|
Mold Temperature
|
85.0 to 215
|
°F
|
|
| Injection Notes | |||
|
This data represents typical values that have been calculated from all products classified as: Generic PUR, Unspecified
This information is provided for comparative purposes only. |
|||
| Extrusion |
Nominal Value
|
Unit
|
|
|
Cylinder Zone 1 Temp.
|
170 to 420
|
°F
|
|
|
Cylinder Zone 2 Temp.
|
185 to 435
|
°F
|
|
|
Cylinder Zone 3 Temp.
|
190 to 450
|
°F
|
|
|
Melt Temperature
|
175 to 460
|
°F
|
|
|
Die Temperature
|
175 to 460
|
°F
|
|
| Extrusion Notes | |||
|
This data represents typical values that have been calculated from all products classified as: Generic PUR, Unspecified
This information is provided for comparative purposes only. |
|||
| Notes |
| 1Typical properties: these are not to be construed as specifications. |