| Product Description | ||||
|
This data represents typical values that have been calculated from all products classified as: Generic SAN
This information is provided for comparative purposes only. |
||||
| General | ||||
|
Material Status
|
|
|||
|
Availability
|
|
|||
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Specific Gravity
|
|||
|
--
|
1.04 to 1.09
|
|
ASTM D792 |
|
73°F
|
1.07 to 1.08
|
g/cm³
|
ISO 1183 |
|
--
|
0.0390
|
lb/in³
|
ISO 1183 2 |
|
Apparent Density
|
|||
|
--
|
0.60 to 0.70
|
g/cm³
|
ASTM D1895 |
|
--
|
0.60 to 0.69
|
g/cm³
|
ISO 60 |
|
Melt Mass-Flow Rate (MFR)
|
|||
|
230°C/3.8 kg
|
3.3 to 26
|
g/10 min
|
ASTM D1238 |
|
220°C/10.0 kg
|
2.6 to 37
|
g/10 min
|
ISO 1133 |
|
Melt Volume-Flow Rate (MVR)
|
|||
|
220°C/10.0 kg
|
0.345 to 3.67
|
in³/10min
|
ISO 1133 |
|
--
|
0.953
|
in³/10min
|
ISO 1133 2 |
|
Molding Shrinkage
|
|||
|
Flow: 73°F
|
0.0035 to 0.0051
|
in/in
|
ASTM D955 |
|
73°F
|
0.35 to 0.51
|
%
|
ISO 294-4 |
|
Water Absorption
|
|||
|
73°F, 24 hr
|
0.30 to 0.31
|
%
|
ASTM D570 |
|
73°F, 24 hr
|
0.30
|
%
|
ISO 62 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus
|
|||
|
73°F
|
450000 to 554000
|
psi
|
ASTM D638 |
|
73°F
|
499000 to 564000
|
psi
|
ISO 527-2 |
|
--
|
512000
|
psi
|
ISO 527-2 2 |
|
Tensile Strength
|
|||
|
Yield, 73°F
|
9240 to 11500
|
psi
|
ASTM D638 |
|
Yield, 73°F
|
9970 to 11500
|
psi
|
ISO 527-2 |
|
Break, 73°F
|
9610 to 11500
|
psi
|
ASTM D638 |
|
Break, 73°F
|
8210 to 11700
|
psi
|
ISO 527-2 |
|
73°F
|
8790 to 14000
|
psi
|
ASTM D638 |
|
Tensile Elongation
|
|||
|
Yield, 73°F
|
2.5 to 4.1
|
%
|
ASTM D638 |
|
Break, 73°F
|
1.7 to 6.7
|
%
|
ASTM D638 |
|
Break, 73°F
|
1.9 to 3.6
|
%
|
ISO 527-2 |
|
Flexural Modulus
|
|||
|
73°F
|
441000 to 658000
|
psi
|
ASTM D790 |
|
73°F
|
448000 to 571000
|
psi
|
ISO 178 |
|
Flexural Strength
|
|||
|
73°F
|
12600 to 18200
|
psi
|
ASTM D790 |
|
73°F
|
12100 to 19200
|
psi
|
ISO 178 |
|
Yield, 73°F
|
12800 to 17900
|
psi
|
ASTM D790 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength (73°F)
|
0.52 to 0.97
|
ft·lb/in²
|
ISO 179 |
|
Charpy Unnotched Impact Strength (73°F)
|
5.1 to 10
|
ft·lb/in²
|
ISO 179 |
|
Notched Izod Impact
|
|||
|
73°F
|
0.18 to 0.55
|
ft·lb/in
|
ASTM D256 |
|
73°F
|
0.48 to 1.9
|
ft·lb/in²
|
ISO 180 |
|
Unnotched Izod Impact
|
|||
|
73°F
|
3.0 to 9.8
|
ft·lb/in
|
ASTM D256 |
|
73°F
|
5.7 to 9.5
|
ft·lb/in²
|
ISO 180 |
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Rockwell Hardness
|
|||
|
73°F
|
83 to 125
|
|
ASTM D785 |
|
73°F
|
82 to 86
|
|
ISO 2039-2 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load
|
|||
|
66 psi, Unannealed
|
204 to 210
|
°F
|
ASTM D648 |
|
66 psi, Unannealed
|
188 to 217
|
°F
|
ISO 75-2/B |
|
264 psi, Unannealed
|
177 to 207
|
°F
|
ASTM D648 |
|
264 psi, Unannealed
|
181 to 219
|
°F
|
ISO 75-2/A |
|
264 psi, Annealed
|
206 to 218
|
°F
|
ASTM D648 |
|
Vicat Softening Temperature
|
|||
|
--
|
200 to 230
|
°F
|
ASTM D1525 |
|
--
|
209 to 230
|
°F
|
ISO 306 |
|
50°C/h, B (50N)
|
216
|
°F
|
ISO 306 2 |
|
CLTE - Flow
|
|||
|
--
|
0.000033 to 0.000039
|
in/in/°F
|
ASTM D696 |
|
--
|
0.000038 to 0.000039
|
in/in/°F
|
ISO 11359-2 |
| Electrical |
Nominal Value
|
Unit
|
Test Method
|
|
Surface Resistivity
|
9.8E+14 to 1.0E+15
|
ohm
|
IEC 60093 |
|
Volume Resistivity (73°F)
|
7.6E+14 to 1.0E+16
|
ohm·cm
|
IEC 60093 |
|
Dielectric Strength
|
|||
|
73°F
|
550 to 890
|
V/mil
|
ASTM D149 |
|
73°F
|
230 to 880
|
V/mil
|
IEC 60243-1 |
|
Dielectric Constant (73°F)
|
2.70 to 3.00
|
|
IEC 60250 |
|
Dissipation Factor (73°F)
|
0.00010 to 0.0080
|
|
IEC 60250 |
| Optical |
Nominal Value
|
Unit
|
Test Method
|
|
Transmittance
|
86.2 to 90.8
|
%
|
ASTM D1003 |
|
Haze
|
0.40 to 2.8
|
%
|
ASTM D1003 |
| Injection |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
170 to 185
|
°F
|
|
|
Drying Time
|
1.9 to 4.0
|
hr
|
|
|
Suggested Max Moisture
|
0.010 to 0.20
|
%
|
|
|
Rear Temperature
|
338 to 448
|
°F
|
|
|
Middle Temperature
|
374 to 447
|
°F
|
|
|
Front Temperature
|
391 to 450
|
°F
|
|
|
Nozzle Temperature
|
383 to 446
|
°F
|
|
|
Processing (Melt) Temp
|
400 to 483
|
°F
|
|
|
Mold Temperature
|
120 to 159
|
°F
|
|
|
Injection Pressure
|
580 to 15500
|
psi
|
|
|
Back Pressure
|
12.5 to 172
|
psi
|
|
|
Clamp Tonnage
|
2.5 to 3.5
|
tons/in²
|
|
| Injection Notes | |||
|
This data represents typical values that have been calculated from all products classified as: Generic SAN
This information is provided for comparative purposes only. |
|||
| Notes |
| 1Typical properties: these are not to be construed as specifications. |
| 2Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |