| Product Description | ||||
|
This data represents typical values that have been calculated from all products classified as: Generic SMA
This information is provided for comparative purposes only. |
||||
| General | ||||
|
Material Status
|
|
|||
|
Availability
|
|
|||
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density (73°F)
|
1.05 to 1.17
|
g/cm³
|
ISO 1183 |
|
Apparent Density
|
0.60
|
g/cm³
|
ASTM D1895 |
|
Melt Mass-Flow Rate (MFR) (240°C/10.0 kg)
|
20 to 22
|
g/10 min
|
ISO 1133 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus (73°F)
|
290000 to 479000
|
psi
|
ISO 527-2 |
|
Tensile Stress
|
ISO 527-2 | ||
|
Yield, 73°F
|
4350 to 6380
|
psi
|
|
|
Break, 73°F
|
4350 to 4940
|
psi
|
|
|
Flexural Modulus (73°F)
|
290000 to 334000
|
psi
|
ISO 178 |
|
Flexural Strength (73°F)
|
8270 to 9020
|
psi
|
ISO 178 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Notched Izod Impact Strength (73°F)
|
3.5 to 9.5
|
ft·lb/in²
|
ISO 180 |
|
Instrumented Dart Impact (73°F)
|
62.0 to 274
|
in·lb
|
ASTM D3763 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Glass Transition Temperature (DSC)
|
264 to 320
|
°F
|
DSC |
|
Vicat Softening Temperature
|
229 to 312
|
°F
|
ISO 306 |
| Extrusion |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
185
|
°F
|
|
|
Drying Time
|
2.5
|
hr
|
|
|
Melt Temperature
|
491 to 493
|
°F
|
|
| Extrusion Notes | |||
|
This data represents typical values that have been calculated from all products classified as: Generic SMA
This information is provided for comparative purposes only. |
|||
| Notes |
| 1Typical properties: these are not to be construed as specifications. |