| Product Description | ||||
|
This data represents typical values that have been calculated from all products classified as: Generic TP, Unspecified
This information is provided for comparative purposes only. |
||||
| General | ||||
|
Material Status
|
|
|||
|
Availability
|
|
|||
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Specific Gravity
|
|||
|
--
|
0.813 to 1.60
|
|
ASTM D792 |
|
73°F
|
0.550 to 1.62
|
g/cm³
|
ISO 1183 |
|
--
|
1.08 to 1.23
|
g/cm³
|
ASTM D1505 |
|
Apparent Density
|
0.52 to 0.72
|
g/cm³
|
ASTM D1895 |
|
Melt Mass-Flow Rate (MFR)
|
|||
|
300°C/1.2 kg
|
0.50 to 45
|
g/10 min
|
ASTM D1238 |
|
150°C/21.6 kg
|
4.0 to 16
|
g/10 min
|
ISO 1133 |
|
Molding Shrinkage
|
|||
|
Flow: 73°F
|
0.00050 to 0.0042
|
in/in
|
ASTM D955 |
|
73°F
|
0.20 to 1.7
|
%
|
ISO 294-4 |
|
Water Absorption (73°F, 24 hr)
|
0.010 to 0.14
|
%
|
ASTM D570 |
|
Environmental Stress-Cracking Resistance (73°F)
|
504 to 720
|
hr
|
ASTM D1693 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus
|
|||
|
73°F
|
110 to 465000
|
psi
|
ASTM D638 |
|
73°F
|
2.00E+6 to 2.70E+6
|
psi
|
ISO 527-2 |
|
Tensile Strength
|
|||
|
Yield, 73°F
|
3070 to 10700
|
psi
|
ASTM D638 |
|
Yield, 73°F
|
4.00 to 5350
|
psi
|
ISO 527-2 |
|
Break, 73°F
|
319 to 5500
|
psi
|
ASTM D638 |
|
Break, 73°F
|
319 to 42100
|
psi
|
ISO 527-2 |
|
73°F
|
125 to 11100
|
psi
|
ASTM D638 |
|
Tensile Elongation
|
|||
|
Yield, 73°F
|
1.5 to 40
|
%
|
ASTM D638 |
|
Break, 73°F
|
0.14 to 30
|
%
|
ASTM D638 |
|
Break, 73°F
|
1.8 to 190
|
%
|
ISO 527-2 |
|
Nominal Tensile Strain at Break (73°F)
|
3.0 to 33
|
%
|
ISO 527-2 |
|
Flexural Modulus
|
|||
|
73°F
|
7300 to 480000
|
psi
|
ASTM D790 |
|
73°F
|
212000 to 2.60E+6
|
psi
|
ISO 178 |
|
Flexural Strength
|
|||
|
73°F
|
297 to 18200
|
psi
|
ASTM D790 |
|
73°F
|
4930 to 62300
|
psi
|
ISO 178 |
|
Yield, 73°F
|
2590 to 17800
|
psi
|
ASTM D790 |
|
Compressive Strength (73°F)
|
14100 to 25400
|
psi
|
ASTM D695 |
| Elastomers |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Stress
|
|||
|
Yield, 73°F
|
1520 to 2180
|
psi
|
ISO 37 |
|
Break, 73°F
|
580 to 2400
|
psi
|
ASTM D412 |
|
Tensile Elongation
|
|||
|
Break, 73°F
|
130 to 510
|
%
|
ASTM D412 |
|
Break, 73°F
|
150 to 200
|
%
|
ISO 37 |
|
Tear Strength (73°F)
|
28.6 to 660
|
lbf/in
|
ASTM D624 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength (73°F)
|
0.95 to 17
|
ft·lb/in²
|
ISO 179 |
|
Charpy Unnotched Impact Strength (73°F)
|
42 to 48
|
ft·lb/in²
|
ISO 179 |
|
Notched Izod Impact (73°F)
|
0.18 to 2.4
|
ft·lb/in
|
ASTM D256 |
|
Unnotched Izod Impact (73°F)
|
0.55 to 9.4
|
ft·lb/in
|
ASTM D256 |
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Rockwell Hardness
|
|||
|
73°F
|
34 to 126
|
|
ASTM D785 |
|
73°F
|
72 to 108
|
|
ISO 2039-2 |
|
Durometer Hardness
|
|||
|
73°F
|
45 to 96
|
|
ASTM D2240 |
|
73°F
|
40 to 88
|
|
ISO 868 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load
|
|||
|
66 psi, Unannealed
|
122 to 271
|
°F
|
ASTM D648 |
|
66 psi, Unannealed
|
192 to 572
|
°F
|
ISO 75-2/B |
|
264 psi, Unannealed
|
101 to 259
|
°F
|
ASTM D648 |
|
Brittleness Temperature
|
-40.7 to -39.1
|
°F
|
ASTM D746 |
|
Glass Transition Temperature
|
|||
|
--
|
-65.2 to 220
|
°F
|
ASTM E1356 |
|
--
|
-40.0 to 340
|
°F
|
DSC |
|
Vicat Softening Temperature
|
200 to 206
|
°F
|
ASTM D1525 |
|
Melting Temperature
|
397 to 506
|
°F
|
|
|
CLTE - Flow
|
|||
|
--
|
0.000016 to 0.00011
|
in/in/°F
|
ASTM D696 |
|
--
|
0.000017 to 0.000085
|
in/in/°F
|
ASTM E831 |
|
Thermal Conductivity (73°F)
|
1.5 to 1.6
|
Btu·in/hr/ft²/°F
|
ASTM C177 |
| Aging |
Nominal Value
|
Unit
|
Test Method
|
|
Change in Tensile Stress (73°F)
|
-27 to 0.0
|
%
|
ISO 1817 |
|
Change in Tensile Strain at Break (73°F)
|
-17 to 17
|
%
|
ISO 1817 |
| Electrical |
Nominal Value
|
Unit
|
Test Method
|
|
Surface Resistivity
|
5.0E+3 to 1.3E+15
|
ohm
|
ASTM D257 |
|
Volume Resistivity
|
|||
|
73°F
|
10 to 2.2E+15
|
ohm·cm
|
ASTM D257 |
|
73°F
|
6.0 to 18
|
ohm·cm
|
ASTM D991 |
|
Dielectric Strength (73°F)
|
340 to 400
|
V/mil
|
ASTM D149 |
|
Dielectric Constant (73°F)
|
1.66 to 4.82
|
|
ASTM D150 |
|
Dissipation Factor (73°F)
|
0.00030 to 0.22
|
|
ASTM D150 |
| Flammability |
Nominal Value
|
Unit
|
Test Method
|
|
Oxygen Index
|
|||
|
--
|
27 to 48
|
%
|
ASTM D2863 |
|
--
|
30 to 45
|
%
|
ISO 4589-2 |
| UL |
Nominal Value
|
Unit
|
Test Method
|
|
RTI Str
|
149 to 257
|
°F
|
UL 746 |
|
RTI Imp
|
149 to 257
|
°F
|
UL 746 |
|
RTI Elec
|
149 to 257
|
°F
|
UL 746 |
| Optical |
Nominal Value
|
Unit
|
Test Method
|
|
Refractive Index
|
1.502 to 1.585
|
|
ASTM D542 |
|
Transmittance
|
90.0 to 92.2
|
%
|
ASTM D1003 |
|
Haze
|
0.93 to 1.6
|
%
|
ASTM D1003 |
| Thermoset |
Nominal Value
|
Unit
|
Test Method
|
|
Thermoset Mix Viscosity (73°F)
|
72.0 to 5060
|
cP
|
ASTM D2393 |
|
Demold Time (73°F)
|
5.0 to 450
|
min
|
| Injection |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
159 to 194
|
°F
|
|
|
Drying Time
|
3.0
|
hr
|
|
|
Rear Temperature
|
355 to 418
|
°F
|
|
|
Middle Temperature
|
365 to 429
|
°F
|
|
|
Front Temperature
|
378 to 445
|
°F
|
|
|
Processing (Melt) Temp
|
387 to 443
|
°F
|
|
|
Mold Temperature
|
75.0 to 118
|
°F
|
|
|
Back Pressure
|
50.0 to 125
|
psi
|
|
|
Screw Speed
|
60 to 61
|
rpm
|
|
| Injection Notes | |||
|
This data represents typical values that have been calculated from all products classified as: Generic TP, Unspecified
This information is provided for comparative purposes only. |
|||
| Extrusion |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
140 to 149
|
°F
|
|
|
Drying Time
|
2.0 to 6.0
|
hr
|
|
|
Cylinder Zone 1 Temp.
|
274 to 355
|
°F
|
|
|
Cylinder Zone 2 Temp.
|
283 to 321
|
°F
|
|
|
Cylinder Zone 3 Temp.
|
291 to 295
|
°F
|
|
|
Cylinder Zone 4 Temp.
|
299 to 302
|
°F
|
|
|
Cylinder Zone 5 Temp.
|
317 to 321
|
°F
|
|
|
Melt Temperature
|
262 to 440
|
°F
|
|
|
Die Temperature
|
328 to 400
|
°F
|
|
| Extrusion Notes | |||
|
This data represents typical values that have been calculated from all products classified as: Generic TP, Unspecified
This information is provided for comparative purposes only. |
|||
| Notes |
| 1Typical properties: these are not to be construed as specifications. |