| Product Description | ||||
|
This data represents typical values that have been calculated from all products classified as: Generic ASA
This information is provided for comparative purposes only. |
||||
| General | ||||
|
Material Status
|
|
|||
|
Availability
|
|
|||
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Specific Gravity
|
|||
|
--
|
1.06 to 1.08
|
|
ASTM D792 |
|
73°F
|
1.04 to 1.10
|
g/cm³
|
ISO 1183 |
|
Melt Mass-Flow Rate (MFR)
|
|||
|
220°C/10.0 kg
|
2.9 to 19
|
g/10 min
|
ASTM D1238 |
|
220°C/10.0 kg
|
5.7 to 27
|
g/10 min
|
ISO 1133 |
|
Melt Volume-Flow Rate (MVR) (220°C/10.0 kg)
|
0.244 to 0.940
|
in³/10min
|
ISO 1133 |
|
Molding Shrinkage
|
|||
|
Flow: 73°F
|
0.0050 to 0.0061
|
in/in
|
ASTM D955 |
|
73°F
|
0.49 to 0.60
|
%
|
ISO 294-4 |
|
Water Absorption
|
|||
|
73°F, 24 hr
|
0.24 to 0.35
|
%
|
ASTM D570 |
|
73°F, 24 hr
|
0.30 to 0.45
|
%
|
ISO 62 |
|
Saturation, 73°F
|
0.49 to 1.7
|
%
|
ISO 62 |
|
Equilibrium, 73°F, 50% RH
|
0.20 to 0.35
|
%
|
ISO 62 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus
|
|||
|
73°F
|
246000 to 392000
|
psi
|
ASTM D638 |
|
73°F
|
260000 to 416000
|
psi
|
ISO 527-2 |
|
Tensile Strength
|
|||
|
Yield, 73°F
|
4990 to 7300
|
psi
|
ASTM D638 |
|
Yield, 73°F
|
5210 to 8050
|
psi
|
ISO 527-2 |
|
Break, 73°F
|
4660 to 5750
|
psi
|
ASTM D638 |
|
Break, 73°F
|
4160 to 8990
|
psi
|
ISO 527-2 |
|
73°F
|
5510 to 7250
|
psi
|
ASTM D638 |
|
Tensile Elongation
|
|||
|
Yield, 73°F
|
2.4 to 6.0
|
%
|
ASTM D638 |
|
Yield, 73°F
|
2.5 to 6.0
|
%
|
ISO 527-2 |
|
Break, 73°F
|
11 to 100
|
%
|
ASTM D638 |
|
Break, 73°F
|
4.0 to 52
|
%
|
ISO 527-2 |
|
Flexural Modulus
|
|||
|
73°F
|
255000 to 377000
|
psi
|
ASTM D790 |
|
73°F
|
272000 to 404000
|
psi
|
ISO 178 |
|
Flexural Strength
|
|||
|
73°F
|
5390 to 11300
|
psi
|
ASTM D790 |
|
73°F
|
7570 to 13500
|
psi
|
ISO 178 |
|
Yield, 73°F
|
7380 to 11400
|
psi
|
ASTM D790 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength (73°F)
|
2.4 to 8.8
|
ft·lb/in²
|
ISO 179 |
|
Charpy Unnotched Impact Strength (73°F)
|
11 to 120
|
ft·lb/in²
|
ISO 179 |
|
Notched Izod Impact
|
|||
|
73°F
|
0.87 to 11
|
ft·lb/in
|
ASTM D256 |
|
73°F
|
2.4 to 12
|
ft·lb/in²
|
ISO 180 |
|
Instrumented Dart Impact (73°F)
|
35.4 to 358
|
in·lb
|
ASTM D3763 |
|
Gardner Impact (73°F)
|
128 to 223
|
in·lb
|
ASTM D3029 |
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Rockwell Hardness
|
|||
|
73°F
|
86 to 110
|
|
ASTM D785 |
|
73°F
|
93 to 118
|
|
ISO 2039-2 |
|
Ball Indentation Hardness
|
9430 to 15200
|
psi
|
ISO 2039-1 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load
|
|||
|
66 psi, Unannealed
|
174 to 225
|
°F
|
ASTM D648 |
|
66 psi, Unannealed
|
188 to 218
|
°F
|
ISO 75-2/B |
|
264 psi, Unannealed
|
170 to 206
|
°F
|
ASTM D648 |
|
264 psi, Unannealed
|
166 to 208
|
°F
|
ISO 75-2/A |
|
264 psi, Annealed
|
181 to 218
|
°F
|
ASTM D648 |
|
Vicat Softening Temperature
|
|||
|
--
|
179 to 237
|
°F
|
ASTM D1525 |
|
--
|
184 to 227
|
°F
|
ISO 306 |
|
Ball Pressure Test
|
Pass
|
|
IEC 60695-10-2 |
|
CLTE
|
|||
|
Flow
|
0.000039 to 0.000059
|
in/in/°F
|
ASTM D696 |
|
Flow
|
0.000046 to 0.000067
|
in/in/°F
|
ASTM E831 |
|
Flow
|
0.000044 to 0.000053
|
in/in/°F
|
ISO 11359-2 |
|
Transverse
|
0.000050 to 0.000072
|
in/in/°F
|
ASTM E831 |
|
Transverse
|
0.000052 to 0.000072
|
in/in/°F
|
ISO 11359-2 |
|
Thermal Conductivity (73°F)
|
1.2
|
Btu·in/hr/ft²/°F
|
ISO 8302 |
| Electrical |
Nominal Value
|
Unit
|
Test Method
|
|
Surface Resistivity
|
1.0E+11 to 1.0E+15
|
ohm
|
ASTM D257, IEC 60093 |
|
Volume Resistivity
|
|||
|
73°F
|
15 to 1.0E+15
|
ohm·cm
|
ASTM D257 |
|
73°F
|
7.6E+13 to 1.0E+14
|
ohm·cm
|
IEC 60093 |
|
Dielectric Strength
|
|||
|
73°F
|
400 to 450
|
V/mil
|
ASTM D149 |
|
73°F
|
410 to 990
|
V/mil
|
IEC 60243-1 |
|
Dielectric Constant
|
|||
|
73°F
|
3.04 to 5.20
|
|
ASTM D150 |
|
73°F
|
3.00 to 3.80
|
|
IEC 60250 |
|
73°F
|
4.18
|
|
IEC 60250 |
|
Dissipation Factor
|
|||
|
73°F
|
0.018 to 0.15
|
|
ASTM D150 |
|
73°F
|
0.0060 to 0.15
|
|
IEC 60250 |
|
Comparative Tracking Index
|
589 to 600
|
V
|
IEC 60112 |
| Flammability |
Nominal Value
|
Unit
|
Test Method
|
|
Glow Wire Flammability Index
|
1200 to 1380
|
°F
|
IEC 60695-2-12 |
|
Glow Wire Ignition Temperature
|
1020 to 1290
|
°F
|
IEC 60695-2-13 |
| Optical |
Nominal Value
|
Unit
|
Test Method
|
|
Gardner Gloss
|
92 to 97
|
|
ASTM D523 |
| Injection |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
175 to 230
|
°F
|
|
|
Drying Time
|
2.9 to 4.2
|
hr
|
|
|
Drying Time, Maximum
|
7.9
|
hr
|
|
|
Suggested Max Moisture
|
0.039 to 0.10
|
%
|
|
|
Suggested Shot Size
|
55 to 60
|
%
|
|
|
Suggested Max Regrind
|
18
|
%
|
|
|
Rear Temperature
|
391 to 476
|
°F
|
|
|
Middle Temperature
|
388 to 493
|
°F
|
|
|
Front Temperature
|
436 to 493
|
°F
|
|
|
Nozzle Temperature
|
419 to 503
|
°F
|
|
|
Processing (Melt) Temp
|
453 to 500
|
°F
|
|
|
Mold Temperature
|
130 to 141
|
°F
|
|
|
Injection Pressure
|
9840 to 15200
|
psi
|
|
|
Back Pressure
|
43.5 to 1460
|
psi
|
|
|
Screw Speed
|
50 to 76
|
rpm
|
|
|
Vent Depth
|
0.0022
|
in
|
|
| Injection Notes | |||
|
This data represents typical values that have been calculated from all products classified as: Generic ASA
This information is provided for comparative purposes only. |
|||
| Extrusion |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
176 to 194
|
°F
|
|
|
Drying Time
|
2.5 to 8.0
|
hr
|
|
|
Suggested Max Moisture
|
0.010 to 0.051
|
%
|
|
|
Cylinder Zone 1 Temp.
|
356 to 410
|
°F
|
|
|
Cylinder Zone 2 Temp.
|
370 to 435
|
°F
|
|
|
Cylinder Zone 3 Temp.
|
379 to 445
|
°F
|
|
|
Cylinder Zone 4 Temp.
|
379 to 455
|
°F
|
|
|
Cylinder Zone 5 Temp.
|
392 to 402
|
°F
|
|
|
Adapter Temperature
|
379 to 455
|
°F
|
|
|
Melt Temperature
|
390 to 473
|
°F
|
|
|
Die Temperature
|
382 to 456
|
°F
|
|
|
Calibration Temp, First
|
105 to 140
|
°F
|
|
| Extrusion Notes | |||
|
This data represents typical values that have been calculated from all products classified as: Generic ASA
This information is provided for comparative purposes only. |
|||
| Notes |
| 1Typical properties: these are not to be construed as specifications. |