| Product Description | ||||
|
This data represents typical values that have been calculated from all products classified as: Generic Biodeg Polymers
This information is provided for comparative purposes only. |
||||
| General | ||||
|
Material Status
|
|
|||
|
Availability
|
|
|||
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Specific Gravity
|
|||
|
--
|
1.13 to 1.46
|
|
ASTM D792 |
|
73°F
|
1.23 to 1.30
|
g/cm³
|
ISO 1183 |
|
--
|
0.990 to 1.35
|
g/cm³
|
ASTM D1505 |
|
Melt Mass-Flow Rate (MFR)
|
|||
|
190°C/2.16 kg
|
0.43 to 20
|
g/10 min
|
ASTM D1238 |
|
190°C/2.16 kg
|
4.4 to 15
|
g/10 min
|
ISO 1133 |
|
Molding Shrinkage - Flow (73°F)
|
0.00024 to 0.015
|
in/in
|
ASTM D955 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus
|
|||
|
73°F
|
90900 to 446000
|
psi
|
ASTM D638 |
|
73°F
|
41800 to 499000
|
psi
|
ISO 527-2 |
|
Tensile Strength
|
|||
|
Yield, 73°F
|
1400 to 5660
|
psi
|
ASTM D638 |
|
Yield, 73°F
|
1310 to 4940
|
psi
|
ISO 527-2 |
|
Break, 73°F
|
969 to 5110
|
psi
|
ASTM D638 |
|
Break, 73°F
|
580 to 4340
|
psi
|
ISO 527-2 |
|
73°F
|
268 to 4690
|
psi
|
ASTM D638 |
|
Tensile Strain
|
|||
|
Yield, 73°F
|
0.70 to 8.2
|
%
|
ISO 527-2 |
|
Break, 73°F
|
1.0 to 23
|
%
|
ASTM D638 |
|
Break, 73°F
|
0.67 to 21
|
%
|
ISO 527-2 |
|
Flexural Modulus
|
|||
|
73°F
|
3380 to 321000
|
psi
|
ASTM D790 |
|
73°F
|
31900 to 517000
|
psi
|
ISO 178 |
|
Flexural Strength (73°F)
|
2390 to 5130
|
psi
|
ISO 178 |
| Films |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Strength - MD (Yield)
|
498 to 6380
|
psi
|
ASTM D882 |
| Elastomers |
Nominal Value
|
Unit
|
Test Method
|
|
Tear Strength (73°F)
|
137 to 851
|
lbf/in
|
ASTM D624 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength (73°F)
|
1.3 to 3.4
|
ft·lb/in²
|
ISO 179 |
|
Charpy Unnotched Impact Strength (73°F)
|
2.3 to 9.2
|
ft·lb/in²
|
ISO 179 |
|
Notched Izod Impact
|
|||
|
73°F
|
0.30 to 1.4
|
ft·lb/in
|
ASTM D256 |
|
73°F
|
4.5 to 17
|
ft·lb/in²
|
ISO 180 |
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Durometer Hardness
|
|||
|
73°F
|
40 to 89
|
|
ASTM D2240 |
|
73°F
|
78 to 81
|
|
ISO 868 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load
|
|||
|
66 psi, Unannealed
|
108 to 246
|
°F
|
ASTM D648 |
|
264 psi, Unannealed
|
102 to 163
|
°F
|
ISO 75-2/A |
|
Vicat Softening Temperature
|
|||
|
--
|
113 to 275
|
°F
|
ASTM D1525 |
|
--
|
208 to 275
|
°F
|
ISO 306 |
|
Melting Temperature
|
|||
|
--
|
187 to 308
|
°F
|
|
|
--
|
192 to 419
|
°F
|
ASTM D3418 |
|
--
|
286 to 290
|
°F
|
ISO 3146 |
| Injection |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
157 to 176
|
°F
|
|
|
Drying Time
|
2.0 to 7.2
|
hr
|
|
|
Suggested Max Moisture
|
0.20 to 2.5
|
%
|
|
|
Rear Temperature
|
113 to 389
|
°F
|
|
|
Middle Temperature
|
158 to 358
|
°F
|
|
|
Front Temperature
|
236 to 347
|
°F
|
|
|
Nozzle Temperature
|
246 to 365
|
°F
|
|
|
Processing (Melt) Temp
|
324 to 383
|
°F
|
|
|
Mold Temperature
|
88.7 to 102
|
°F
|
|
|
Screw Speed
|
80 to 138
|
rpm
|
|
| Injection Notes | |||
|
This data represents typical values that have been calculated from all products classified as: Generic Biodeg Polymers
This information is provided for comparative purposes only. |
|||
| Extrusion |
Nominal Value
|
Unit
|
|
|
Cylinder Zone 1 Temp.
|
246 to 357
|
°F
|
|
|
Cylinder Zone 2 Temp.
|
291 to 356
|
°F
|
|
|
Cylinder Zone 3 Temp.
|
309 to 365
|
°F
|
|
|
Cylinder Zone 4 Temp.
|
291 to 383
|
°F
|
|
|
Cylinder Zone 5 Temp.
|
293 to 374
|
°F
|
|
|
Melt Temperature
|
320 to 383
|
°F
|
|
| Extrusion Notes | |||
|
This data represents typical values that have been calculated from all products classified as: Generic Biodeg Polymers
This information is provided for comparative purposes only. |
|||
| Notes |
| 1Typical properties: these are not to be construed as specifications. |