| Acrylonitrile Ethylene Styrene (AES) Typical Properties |
|
|
|
-
-
-
|
English
|
| Specific Gravity | 1.04 to 1.06 | | Melt Mass Flow Rate (g/10 min) | 3.5 to 65 | | Flexural Modulus (psi) | 290000 to 360000 | | Tensile Strength (psi) | 3980 to 7940 | | Tensile Elongation (%) | 8.9 to 50 | | Rockwell Hardness | 90 to 113 | | Notched Izod Impact (ft·lb/in) | 1.11 to 2.88 | | DTUL at 66 psi (0.45 MPa) (°F) | -- | | DTUL at 264 psi (1.8 MPa) (°F) | 168 to 205 | | CLTE, Flow (in/in/°F) | 0.000039 to 0.000050 |
SI
|
| Specific Gravity (g/cm³) | 1.04 to 1.06 | | Melt Mass Flow Rate (g/10 min) | 3.5 to 65 | | Flexural Modulus (MPa) | 2000 to 2480 | | Tensile Strength (MPa) | 27.5 to 54.7 | | Tensile Elongation (%) | 8.9 to 50 | | Rockwell Hardness | 90 to 113 | | Notched Izod Impact (J/m) | 59.0 to 154 | | DTUL at 66 psi (0.45 MPa) (°C) | -- | | DTUL at 264 psi (1.8 MPa) (°C) | 75.7 to 95.9 | | CLTE, Flow (cm/cm/°C) | 0.000070 to 0.000090 |
|
|