| Acrylonitrile Styrene Acrylate (ASA) Typical Properties |
|
|
|
-
-
-
|
English
|
| Specific Gravity | 1.05 to 1.20 | 1.11 to 1.24 | 1.07 to 1.12 | | Melt Mass Flow Rate (g/10 min) | 0.20 to 2.0 | 0.50 to 35 | 5.0 to 11 | | Flexural Modulus (psi) | 247000 to 405000 | 290000 to 400000 | 253000 to 315000 | | Tensile Strength (psi) | 4150 to 8180 | 6300 to 9210 | 4030 to 6280 | | Tensile Elongation (%) | 2.0 to 5.1 | 3.4 to 100 | 2.5 to 4.4 | | Rockwell Hardness | 86 to 110 | 102 to 116 | -- | | Notched Izod Impact (ft·lb/in) | 0.337 to 6.26 | 0.0131 to 13.2 | 0.553 to 7.49 | | DTUL at 66 psi (0.45 MPa) (°F) | 183 to 216 | 212 to 266 | 187 | | DTUL at 264 psi (1.8 MPa) (°F) | 166 to 206 | 180 to 229 | 167 to 194 | | CLTE, Flow (in/in/°F) | 0.000033 to 12000 | 0.000039 to 0.000045 | 0.000047 to 0.000061 |
SI
|
| Specific Gravity (g/cm³) | 1.05 to 1.20 | 1.11 to 1.24 | 1.07 to 1.12 | | Melt Mass Flow Rate (g/10 min) | 0.20 to 2.0 | 0.50 to 35 | 5.0 to 11 | | Flexural Modulus (MPa) | 1710 to 2790 | 2000 to 2760 | 1750 to 2170 | | Tensile Strength (MPa) | 28.6 to 56.4 | 43.4 to 63.5 | 27.8 to 43.3 | | Tensile Elongation (%) | 2.0 to 5.1 | 3.4 to 100 | 2.5 to 4.4 | | Rockwell Hardness | 86 to 110 | 102 to 116 | -- | | Notched Izod Impact (J/m) | 18.0 to 334 | 0.700 to 706 | 29.5 to 400 | | DTUL at 66 psi (0.45 MPa) (°C) | 83.9 to 102 | 99.8 to 130 | 86.0 | | DTUL at 264 psi (1.8 MPa) (°C) | 74.4 to 96.9 | 82.0 to 110 | 74.8 to 90.0 | | CLTE, Flow (cm/cm/°C) | 0.000060 to 22000 | 0.000071 to 0.000082 | 0.000084 to 0.00011 |
|
|