| Acetal (Acetal) Typical Properties |
|
|
|
-
-
-
|
English
|
| Specific Gravity | 1.40 to 1.43 | 1.42 | | Melt Mass Flow Rate (g/10 min) | 1.4 to 27 | -- | | Flexural Modulus (psi) | 272000 to 428000 | 359000 to 458000 | | Tensile Strength (psi) | 6240 to 9830 | 7620 to 10700 | | Tensile Elongation (%) | 1.0 to 200 | 3.0 to 77 | | Rockwell Hardness | 80 to 117 | 93 to 120 | | Notched Izod Impact (ft·lb/in) | 0.738 to 1.70 | 0.694 to 2.39 | | DTUL at 66 psi (0.45 MPa) (°F) | 309 to 322 | 320 to 342 | | DTUL at 264 psi (1.8 MPa) (°F) | 211 to 232 | 196 to 277 | | CLTE, Flow (in/in/°F) | 5.6E-6 to 0.14 | 0.000055 to 0.000067 |
SI
|
| Specific Gravity (g/cm³) | 1.40 to 1.43 | 1.41 to 1.42 | | Melt Mass Flow Rate (g/10 min) | 1.4 to 27 | -- | | Flexural Modulus (MPa) | 1880 to 2950 | 2480 to 3160 | | Tensile Strength (MPa) | 43.0 to 67.8 | 52.5 to 73.5 | | Tensile Elongation (%) | 1.0 to 200 | 3.0 to 77 | | Rockwell Hardness | 80 to 117 | 93 to 120 | | Notched Izod Impact (J/m) | 39.4 to 90.5 | 37.0 to 128 | | DTUL at 66 psi (0.45 MPa) (°C) | 154 to 161 | 160 to 172 | | DTUL at 264 psi (1.8 MPa) (°C) | 99.3 to 111 | 91.0 to 136 | | CLTE, Flow (cm/cm/°C) | 0.000010 to 0.25 | 0.000100 to 0.00012 |
|
|