| Acrylic (Acrylic) Typical Properties |
|
|
|
-
-
-
|
English
|
| Specific Gravity | 1.16 to 1.20 | 1.05 to 1.09 | 1.11 to 1.19 | 1.34 to 1.35 | | Melt Mass Flow Rate (g/10 min) | 0.30 to 4.6 | 0.40 to 9.1 | -- | 34 | | Flexural Modulus (psi) | 162000 to 523000 | 264000 to 493000 | 210000 to 500000 | 293000 to 372000 | | Tensile Strength (psi) | 5310 to 11800 | 4000 to 9290 | 3800 to 10200 | 5740 to 6160 | | Tensile Elongation (%) | 0.0 to 7.3 | 2.0 to 59 | 2.7 to 250 | 55 to 170 | | Rockwell Hardness | 44 to 102 | 61 to 86 | 54 to 123 | 87 to 111 | | Notched Izod Impact (ft·lb/in) | 0.169 to 1.13 | 0.340 to 3.00 | 0.397 to 1.32 | 0.600 to 18.0 | | DTUL at 66 psi (0.45 MPa) (°F) | 174 to 219 | 172 to 199 | 167 to 203 | 162 to 178 | | DTUL at 264 psi (1.8 MPa) (°F) | 168 to 223 | 187 to 201 | 153 to 221 | 151 to 174 | | CLTE, Flow (in/in/°F) | 0.000025 to 0.000061 | -- | 0.000034 to 0.000059 | 0.000038 to 0.000045 |
SI
|
| Specific Gravity (g/cm³) | 1.15 to 1.19 | 1.04 to 1.09 | 1.11 to 1.19 | 1.34 to 1.35 | | Melt Mass Flow Rate (g/10 min) | 0.30 to 4.6 | 0.40 to 9.1 | -- | 34 | | Flexural Modulus (MPa) | 1120 to 3610 | 1820 to 3400 | 1450 to 3450 | 2020 to 2560 | | Tensile Strength (MPa) | 36.6 to 81.1 | 27.6 to 64.0 | 26.2 to 70.3 | 39.6 to 42.5 | | Tensile Elongation (%) | 0.0 to 7.3 | 2.0 to 59 | 2.7 to 250 | 55 to 170 | | Rockwell Hardness | 44 to 102 | 61 to 86 | 54 to 123 | 87 to 111 | | Notched Izod Impact (J/m) | 9.03 to 60.2 | 18.1 to 160 | 21.2 to 70.7 | 32.0 to 961 | | DTUL at 66 psi (0.45 MPa) (°C) | 78.7 to 104 | 77.8 to 92.8 | 75.0 to 95.0 | 72.2 to 81.1 | | DTUL at 264 psi (1.8 MPa) (°C) | 75.6 to 106 | 86.2 to 94.1 | 67.2 to 105 | 65.9 to 79.1 | | CLTE, Flow (cm/cm/°C) | 0.000045 to 0.00011 | -- | 0.000062 to 0.00011 | 0.000069 to 0.000081 |
|
|