| Dicyclopentadiene (DCPD) Typical Properties |
|
|
|
-
-
-
|
English
|
| Specific Gravity | 1.03 to 1.04 | | Melt Mass Flow Rate (g/10 min) | -- | | Flexural Modulus (psi) | 259000 to 275000 | | Tensile Strength (psi) | 6220 to 6790 | | Tensile Elongation (%) | 4.0 to 5.7 | | Rockwell Hardness | 112 to 114 | | Notched Izod Impact (ft·lb/in) | 1.83 to 9.25 | | DTUL at 66 psi (0.45 MPa) (°F) | -- | | DTUL at 264 psi (1.8 MPa) (°F) | 225 to 248 | | CLTE, Flow (in/in/°F) | 0.000046 to 0.000050 |
SI
|
| Specific Gravity (g/cm³) | 1.02 to 1.04 | | Melt Mass Flow Rate (g/10 min) | -- | | Flexural Modulus (MPa) | 1780 to 1900 | | Tensile Strength (MPa) | 42.9 to 46.8 | | Tensile Elongation (%) | 4.0 to 5.7 | | Rockwell Hardness | 112 to 114 | | Notched Izod Impact (J/m) | 97.4 to 494 | | DTUL at 66 psi (0.45 MPa) (°C) | -- | | DTUL at 264 psi (1.8 MPa) (°C) | 107 to 120 | | CLTE, Flow (cm/cm/°C) | 0.000083 to 0.000090 |
|
|