| Epoxy (Epoxy) Typical Properties |
|
|
|
-
-
-
|
English
|
| Specific Gravity | 1.01 to 2.00 | 1.01 to 1.25 | | Melt Mass Flow Rate (g/10 min) | -- | -- | | Flexural Modulus (psi) | 9.96 to 1.80E+6 | 480000 to 600000 | | Tensile Strength (psi) | 0.900 to 10100 | 9810 to 13800 | | Tensile Elongation (%) | 0.40 to 7.9 | 2.8 to 8.0 | | Rockwell Hardness | 109 to 118 | -- | | Notched Izod Impact (ft·lb/in) | 0.00646 to 1.01 | -- | | DTUL at 66 psi (0.45 MPa) (°F) | 119 to 470 | 245 | | DTUL at 264 psi (1.8 MPa) (°F) | 75.0 to 480 | 203 to 302 | | CLTE, Flow (in/in/°F) | 3.2E-6 to 4.2 | 0.000017 to 0.000065 |
SI
|
| Specific Gravity (g/cm³) | 1.01 to 2.00 | 1.01 to 1.25 | | Melt Mass Flow Rate (g/10 min) | -- | -- | | Flexural Modulus (MPa) | 0.0686 to 12400 | 3310 to 4140 | | Tensile Strength (MPa) | 0.00621 to 69.8 | 67.6 to 95.1 | | Tensile Elongation (%) | 0.40 to 7.9 | 2.8 to 8.0 | | Rockwell Hardness | 109 to 118 | -- | | Notched Izod Impact (J/m) | 0.345 to 53.7 | -- | | DTUL at 66 psi (0.45 MPa) (°C) | 48.1 to 243 | 118 | | DTUL at 264 psi (1.8 MPa) (°C) | 23.9 to 249 | 95.0 to 150 | | CLTE, Flow (cm/cm/°C) | 5.8E-6 to 7.5 | 0.000031 to 0.00012 |
|
|