| Fluoropolymer (Fluoropolymer) Typical Properties |
|
|
|
-
-
-
|
English
|
| Specific Gravity | 1.70 to 1.74 | 2.14 to 2.15 | 1.80 to 1.90 | 1.38 to 1.63 | 1.05 to 2.80 | 2.08 to 2.13 | 2.14 to 2.15 | 2.03 to 2.13 | 1.49 to 2.24 | 1.75 to 1.79 | | Melt Mass Flow Rate (g/10 min) | 2.3 to 30 | 1.0 to 22 | 8.9 to 20 | -- | 5.0 to 38 | -- | -- | 2.3 to 2.5 | -- | -- | | Flexural Modulus (psi) | 92000 to 203000 | 75500 to 98600 | 522 to 2290 | -- | 30000 to 261000 | 233000 to 238000 | 7300 to 100000 | -- | 27000 to 501000 | 29000 to 325000 | | Tensile Strength (psi) | 500 to 7070 | 2900 to 4530 | 1260 to 2860 | 125 to 1930 | 609 to 6690 | 3690 to 9270 | 1910 to 4140 | 1970 to 3100 | 1920 to 5110 | 1610 to 8450 | | Tensile Elongation (%) | 200 to 600 | 0.80 to 400 | 160 to 330 | 240 to 480 | 7.9 to 450 | 98 to 250 | 270 to 300 | 120 to 300 | 190 to 400 | 3.5 to 59 | | Rockwell Hardness | -- | -- | -- | -- | 98 to 103 | -- | -- | -- | -- | 100 | | Notched Izod Impact (ft·lb/in) | -- | 4.00 | -- | -- | -- | 3.50 | -- | -- | 3.00 to 3.08 | 1.01 to 3.34 | | DTUL at 66 psi (0.45 MPa) (°F) | 219 to 220 | 158 | -- | -- | 313 to 392 | 219 to 258 | 164 | -- | 250 | 117 to 299 | | DTUL at 264 psi (1.8 MPa) (°F) | 164 to 166 | 124 | -- | -- | 309 to 345 | 167 | 118 | -- | 132 to 133 | 95.6 to 240 | | CLTE, Flow (in/in/°F) | 0.000050 to 0.000074 | 0.000052 to 0.000055 | -- | -- | 0.00014 to 0.00017 | 0.000026 | 0.000088 to 0.000093 | 0.000089 | 0.000028 to 0.17 | 0.000065 to 0.000090 |
SI
|
| Specific Gravity (g/cm³) | 1.69 to 1.74 | 2.13 to 2.15 | 1.79 to 1.90 | 1.37 to 1.62 | 1.05 to 2.79 | 2.07 to 2.12 | 2.14 to 2.15 | 2.03 to 2.13 | 1.49 to 2.24 | 1.74 to 1.79 | | Melt Mass Flow Rate (g/10 min) | 2.3 to 30 | 1.0 to 22 | 8.9 to 20 | -- | 5.0 to 38 | -- | -- | 2.3 to 2.5 | -- | -- | | Flexural Modulus (MPa) | 634 to 1400 | 521 to 680 | 3.60 to 15.8 | -- | 207 to 1800 | 1600 to 1640 | 50.3 to 690 | -- | 186 to 3460 | 200 to 2240 | | Tensile Strength (MPa) | 3.45 to 48.7 | 20.0 to 31.2 | 8.67 to 19.7 | 0.862 to 13.3 | 4.20 to 46.1 | 25.4 to 63.9 | 13.2 to 28.6 | 13.6 to 21.3 | 13.2 to 35.2 | 11.1 to 58.3 | | Tensile Elongation (%) | 200 to 600 | 0.80 to 400 | 160 to 330 | 240 to 480 | 7.9 to 450 | 98 to 250 | 270 to 300 | 120 to 300 | 190 to 400 | 3.5 to 59 | | Rockwell Hardness | -- | -- | -- | -- | 98 to 103 | -- | -- | -- | -- | 100 | | Notched Izod Impact (J/m) | -- | 214 | -- | -- | -- | 187 | -- | -- | 160 to 164 | 54.1 to 179 | | DTUL at 66 psi (0.45 MPa) (°C) | 104 | 70.0 | -- | -- | 156 to 200 | 104 to 126 | 73.3 | -- | 121 | 47.2 to 149 | | DTUL at 264 psi (1.8 MPa) (°C) | 73.3 to 74.7 | 51.1 | -- | -- | 154 to 174 | 75.0 | 47.8 | -- | 55.5 to 56.0 | 35.3 to 116 | | CLTE, Flow (cm/cm/°C) | 0.000090 to 0.00013 | 0.000093 to 0.000099 | -- | -- | 0.00026 to 0.00030 | 0.000047 | 0.00016 to 0.00017 | 0.00016 | 0.000050 to 0.31 | 0.00012 to 0.00016 |
|
|