| Liquid Crystal Polymer (LCP) Typical Properties |
|
|
|
-
-
-
|
English
|
| Specific Gravity | 1.38 to 2.71 | | Melt Mass Flow Rate (g/10 min) | 14 | | Flexural Modulus (psi) | 1.26E+6 to 2.88E+6 | | Tensile Strength (psi) | 6500 to 26800 | | Tensile Elongation (%) | 0.40 to 3.5 | | Rockwell Hardness | 53 to 105 | | Notched Izod Impact (ft·lb/in) | 0.367 to 1.52 | | DTUL at 66 psi (0.45 MPa) (°F) | 527 to 572 | | DTUL at 264 psi (1.8 MPa) (°F) | 368 to 564 | | CLTE, Flow (in/in/°F) | 2.1E-6 to 5.8E-6 |
SI
|
| Specific Gravity (g/cm³) | 1.38 to 2.70 | | Melt Mass Flow Rate (g/10 min) | 14 | | Flexural Modulus (MPa) | 8720 to 19900 | | Tensile Strength (MPa) | 44.8 to 185 | | Tensile Elongation (%) | 0.40 to 3.5 | | Rockwell Hardness | 53 to 105 | | Notched Izod Impact (J/m) | 19.6 to 81.3 | | DTUL at 66 psi (0.45 MPa) (°C) | 275 to 300 | | DTUL at 264 psi (1.8 MPa) (°C) | 187 to 295 | | CLTE, Flow (cm/cm/°C) | 3.8E-6 to 0.000010 |
|
|