| Maleic Anhydride Grafted Polymer (MAH-g) Typical Properties |
|
|
|
-
-
-
|
English
|
| Specific Gravity | 0.875 to 0.962 | | Melt Mass Flow Rate (g/10 min) | 1.0 to 12 | | Flexural Modulus (psi) | 2000 to 134000 | | Tensile Strength (psi) | 1200 to 2410 | | Tensile Elongation (%) | 100 to 2000 | | Rockwell Hardness | -- | | Notched Izod Impact (ft·lb/in) | -- | | DTUL at 66 psi (0.45 MPa) (°F) | -- | | DTUL at 264 psi (1.8 MPa) (°F) | -- | | CLTE, Flow (in/in/°F) | -- |
SI
|
| Specific Gravity (g/cm³) | 0.873 to 0.960 | | Melt Mass Flow Rate (g/10 min) | 1.0 to 12 | | Flexural Modulus (MPa) | 13.8 to 924 | | Tensile Strength (MPa) | 8.30 to 16.6 | | Tensile Elongation (%) | 100 to 2000 | | Rockwell Hardness | -- | | Notched Izod Impact (J/m) | -- | | DTUL at 66 psi (0.45 MPa) (°C) | -- | | DTUL at 264 psi (1.8 MPa) (°C) | -- | | CLTE, Flow (cm/cm/°C) | -- |
|
|