| Polyamide (Nylon) Typical Properties |
|
|
|
-
-
-
|
English
|
| Specific Gravity | -- | 1.03 to 1.05 | 0.980 to 1.23 | 1.01 to 1.03 | 1.17 to 1.20 | 0.922 to 1.17 | 1.03 to 1.14 | 1.03 to 1.04 | 1.12 | 1.16 to 1.18 | 1.06 to 1.08 | 1.07 to 1.17 | 1.06 to 1.35 | 0.994 to 1.23 | 1.04 to 1.14 | 1.09 to 1.15 | -- | 1.14 | 1.10 to 1.21 | 0.992 to 1.20 | 0.959 to 1.06 | 1.08 to 1.27 | 1.08 to 1.13 | -- | 1.10 to 1.16 | | Melt Mass Flow Rate (g/10 min) | -- | -- | -- | 7.0 to 20 | -- | -- | -- | 6.0 to 7.0 | -- | -- | 6.0 to 7.0 | -- | -- | 10 | 10 | -- | -- | -- | -- | 0.52 to 6.5 | 1.0 to 7.5 | 4.0 to 40 | 3.0 | -- | 20 to 310 | | Flexural Modulus (psi) | -- | 41800 to 200000 | 16000 to 334000 | 17600 to 47400 | 50800 to 490000 | 290 to 453000 | 384000 to 439000 | 10000 to 508000 | -- | 421000 | 145000 to 315000 | 180000 to 315000 | 43500 to 409000 | 170000 to 510000 | 290000 to 452000 | 92500 to 471000 | -- | 435000 | 294000 to 1.16E+6 | 43500 to 510000 | 126000 to 319000 | 277000 to 345000 | 63500 to 68100 | -- | 219000 to 536000 | | Tensile Strength (psi) | -- | 5740 to 10000 | 2180 to 8690 | 1160 to 7040 | 4350 to 14600 | 2810 to 12900 | 3150 to 12300 | 870 to 12600 | 13000 to 13100 | 12300 to 14500 | 4330 to 6620 | 5780 to 9020 | 1310 to 28500 | 5000 to 14000 | 7250 to 12900 | 3340 to 13000 | -- | 13100 | 2900 to 23200 | 2870 to 16200 | 3190 to 7400 | 6350 to 9950 | 7500 to 8420 | -- | 7390 to 12400 | | Tensile Elongation (%) | -- | 5.0 to 58 | 0.40 to 210 | 17 to 400 | 0.56 to 53 | 0.50 to 50 | 4.0 to 64 | 20 to 270 | 7.4 to 51 | 8.0 to 300 | 3.2 to 100 | 3.3 to 300 | 2.5 to 70 | 0.70 to 56 | 4.0 to 180 | 1.5 to 50 | -- | 15 | 2.1 to 69 | 2.5 to 200 | 4.0 to 95 | 7.0 to 100 | 300 to 500 | -- | 1.5 to 15 | | Rockwell Hardness | -- | 78 to 108 | 79 to 115 | -- | 90 to 100 | 101 to 123 | -- | 74 to 120 | -- | -- | 90 to 105 | 90 to 116 | 113 to 115 | 78 to 123 | -- | 112 to 120 | -- | 118 | -- | 119 to 120 | -- | 110 to 115 | -- | -- | 110 to 128 | | Notched Izod Impact (ft·lb/in) | -- | 0.300 to 2.14 | 0.206 to 3.18 | 0.506 to 3.18 | 0.750 to 1.59 | 0.300 to 3.02 | 0.700 to 1.46 | 0.800 to 6.08 | -- | -- | 0.182 to 15.0 | 0.700 to 3.81 | 0.393 to 1.53 | 0.0843 to 3.36 | 0.700 to 1.29 | 0.483 to 2.03 | -- | 0.375 | 1.46 to 1.51 | 0.627 to 1.62 | 2.00 to 15.0 | 0.749 to 4.00 | 1.60 to 16.1 | -- | 0.276 to 18.2 | | DTUL at 66 psi (0.45 MPa) (°F) | -- | 290 to 305 | 175 to 380 | 124 to 240 | 429 to 556 | 295 to 420 | 140 to 374 | 102 to 374 | 282 to 285 | -- | 190 to 387 | 318 to 356 | 117 to 331 | 348 to 465 | 266 to 320 | 296 to 449 | -- | -- | 122 to 410 | 238 to 362 | 140 to 284 | 273 to 374 | -- | -- | 307 to 454 | | DTUL at 264 psi (1.8 MPa) (°F) | -- | 112 to 130 | 104 to 138 | 113 to 114 | 318 to 380 | 119 to 178 | 122 to 167 | 97.9 to 115 | 246 to 249 | 212 | 145 to 305 | 134 to 156 | 128 to 207 | 137 to 203 | 149 to 176 | 112 to 200 | -- | 275 | 118 to 392 | 124 to 300 | 131 | 239 to 294 | -- | -- | 218 to 541 | | CLTE, Flow (in/in/°F) | -- | 0.000047 to 0.000071 | 4.2E-6 to 0.00013 | 0.000050 to 0.00013 | 0.000038 to 0.000050 | 5.6E-6 to 130 | 0.000052 to 0.000094 | 0.000088 to 0.000090 | 0.000028 | 0.000039 | 0.000055 to 0.000056 | 0.000044 to 0.000067 | 0.000026 to 0.000094 | 0.000027 to 0.000078 | 0.000036 | 0.000038 to 0.000054 | -- | -- | 0.000011 to 0.000056 | 0.000012 to 0.000071 | 0.000022 | 0.000044 to 0.000051 | -- | 0.000028 | 0.000025 to 0.000053 |
SI
|
| Specific Gravity (g/cm³) | -- | 1.03 to 1.04 | 0.978 to 1.23 | 1.01 to 1.03 | 1.17 to 1.19 | 0.920 to 1.17 | 1.03 to 1.14 | 1.02 to 1.03 | 1.12 | 1.16 to 1.18 | 1.06 to 1.08 | 1.07 to 1.17 | 1.05 to 1.35 | 0.991 to 1.23 | 1.04 to 1.14 | 1.09 to 1.15 | -- | 1.14 | 1.10 to 1.21 | 0.990 to 1.20 | 0.957 to 1.05 | 1.08 to 1.27 | 1.07 to 1.13 | -- | 1.10 to 1.16 | | Melt Mass Flow Rate (g/10 min) | -- | -- | -- | 7.0 to 20 | -- | -- | -- | 6.0 to 7.0 | -- | -- | 6.0 to 7.0 | -- | -- | 10 | 10 | -- | -- | -- | -- | 0.52 to 6.5 | 1.0 to 7.5 | 4.0 to 40 | 3.0 | -- | 20 to 310 | | Flexural Modulus (MPa) | -- | 288 to 1380 | 110 to 2310 | 121 to 327 | 350 to 3380 | 2.00 to 3130 | 2650 to 3030 | 69.0 to 3500 | -- | 2900 | 1000 to 2170 | 1240 to 2170 | 300 to 2820 | 1170 to 3520 | 2000 to 3110 | 638 to 3250 | -- | 3000 | 2030 to 8000 | 300 to 3520 | 869 to 2200 | 1910 to 2380 | 438 to 469 | -- | 1510 to 3700 | | Tensile Strength (MPa) | -- | 39.6 to 69.0 | 15.0 to 59.9 | 8.00 to 48.6 | 30.0 to 101 | 19.4 to 88.8 | 21.7 to 84.8 | 6.00 to 86.6 | 89.8 to 90.0 | 85.0 to 100.0 | 29.9 to 45.6 | 39.9 to 62.2 | 9.00 to 196 | 34.5 to 96.5 | 50.0 to 88.6 | 23.0 to 89.4 | -- | 90.0 | 20.0 to 160 | 19.8 to 112 | 22.0 to 51.0 | 43.8 to 68.6 | 51.7 to 58.1 | -- | 50.9 to 85.7 | | Tensile Elongation (%) | -- | 5.0 to 58 | 0.40 to 210 | 17 to 400 | 0.56 to 53 | 0.50 to 50 | 4.0 to 64 | 20 to 270 | 7.4 to 51 | 8.0 to 300 | 3.2 to 100 | 3.3 to 300 | 2.5 to 70 | 0.70 to 56 | 4.0 to 180 | 1.5 to 50 | -- | 15 | 2.1 to 69 | 2.5 to 200 | 4.0 to 95 | 7.0 to 100 | 300 to 500 | -- | 1.5 to 15 | | Rockwell Hardness | -- | 78 to 108 | 79 to 115 | -- | 90 to 100 | 101 to 123 | -- | 74 to 120 | -- | -- | 90 to 105 | 90 to 116 | 113 to 115 | 78 to 123 | -- | 112 to 120 | -- | 118 | -- | 119 to 120 | -- | 110 to 115 | -- | -- | 110 to 128 | | Notched Izod Impact (J/m) | -- | 16.0 to 114 | 11.0 to 170 | 27.0 to 170 | 40.0 to 85.1 | 16.0 to 161 | 37.4 to 78.2 | 42.7 to 325 | -- | -- | 9.70 to 801 | 37.4 to 203 | 21.0 to 81.6 | 4.50 to 179 | 37.4 to 69.0 | 25.8 to 109 | -- | 20.0 | 78.1 to 80.3 | 33.5 to 86.4 | 107 to 801 | 40.0 to 214 | 85.4 to 859 | -- | 14.7 to 971 | | DTUL at 66 psi (0.45 MPa) (°C) | -- | 144 to 152 | 79.2 to 193 | 51.0 to 116 | 220 to 291 | 146 to 216 | 60.0 to 190 | 39.0 to 190 | 139 to 140 | -- | 87.8 to 197 | 159 to 180 | 47.2 to 166 | 176 to 241 | 130 to 160 | 146 to 231 | -- | -- | 50.0 to 210 | 115 to 183 | 60.0 to 140 | 134 to 190 | -- | -- | 153 to 234 | | DTUL at 264 psi (1.8 MPa) (°C) | -- | 44.7 to 54.6 | 40.0 to 58.8 | 45.0 to 45.3 | 159 to 193 | 48.3 to 81.4 | 50.0 to 75.0 | 36.6 to 46.4 | 119 to 120 | 100 | 62.5 to 152 | 56.9 to 68.7 | 53.2 to 97.1 | 58.4 to 95.2 | 65.0 to 80.0 | 44.7 to 93.2 | -- | 135 | 48.0 to 200 | 51.3 to 149 | 54.8 to 55.0 | 115 to 145 | -- | -- | 103 to 283 | | CLTE, Flow (cm/cm/°C) | -- | 0.000085 to 0.00013 | 7.5E-6 to 0.00023 | 0.000090 to 0.00024 | 0.000068 to 0.000090 | 0.000010 to 230 | 0.000093 to 0.00017 | 0.00016 | 0.000050 to 0.000051 | 0.000070 | 0.000099 to 0.00010 | 0.000079 to 0.00012 | 0.000047 to 0.00017 | 0.000049 to 0.00014 | 0.000065 | 0.000068 to 0.000098 | -- | -- | 0.000020 to 0.00010 | 0.000022 to 0.00013 | 0.000040 | 0.000079 to 0.000091 | -- | 0.000051 | 0.000045 to 0.000095 |
|
|