| Polybutylene (PB) Typical Properties |
|
|
|
-
-
-
|
English
|
| Specific Gravity | 0.897 to 0.933 | | Melt Mass Flow Rate (g/10 min) | 0.35 to 5.3 | | Flexural Modulus (psi) | 16900 to 65300 | | Tensile Strength (psi) | 1630 to 5170 | | Tensile Elongation (%) | 230 to 360 | | Rockwell Hardness | -- | | Notched Izod Impact (ft·lb/in) | -- | | DTUL at 66 psi (0.45 MPa) (°F) | -- | | DTUL at 264 psi (1.8 MPa) (°F) | -- | | CLTE, Flow (in/in/°F) | 0.000071 |
SI
|
| Specific Gravity (g/cm³) | 0.895 to 0.931 | | Melt Mass Flow Rate (g/10 min) | 0.35 to 5.3 | | Flexural Modulus (MPa) | 117 to 450 | | Tensile Strength (MPa) | 11.3 to 35.7 | | Tensile Elongation (%) | 230 to 360 | | Rockwell Hardness | -- | | Notched Izod Impact (J/m) | -- | | DTUL at 66 psi (0.45 MPa) (°C) | -- | | DTUL at 264 psi (1.8 MPa) (°C) | -- | | CLTE, Flow (cm/cm/°C) | 0.00013 |
|
|