| Polycarbonate (PC) Typical Properties |
|
|
|
-
-
-
|
English
|
| Specific Gravity | 1.17 to 1.22 | 1.14 to 1.22 | 1.15 | 1.18 to 1.24 | 1.20 to 1.22 | 1.20 to 1.21 | 1.20 | 1.21 to 1.22 | 1.20 | | Melt Mass Flow Rate (g/10 min) | 3.8 to 26 | 1.3 to 36 | 1.5 to 15 | 6.2 to 16 | 8.0 to 35 | 4.0 to 22 | 5.6 to 30 | 9.2 to 21 | 2.0 to 3.0 | | Flexural Modulus (psi) | 276000 to 386000 | 281000 to 402000 | 280000 to 361000 | 210000 to 330000 | 266000 to 353000 | 227000 to 338000 | 307000 to 334000 | 4160 to 151000 | 294000 to 341000 | | Tensile Strength (psi) | 7610 to 10200 | 7150 to 9040 | 6000 to 9100 | 5480 to 8850 | 6420 to 8170 | 6660 to 9200 | 8680 to 10200 | 1640 to 6050 | 9380 to 11300 | | Tensile Elongation (%) | 0.0 to 120 | 1.7 to 94 | 3.7 to 11 | 1.5 to 150 | 3.0 to 54 | 2.0 to 150 | 6.0 to 86 | 120 to 180 | 6.0 to 120 | | Rockwell Hardness | 70 to 121 | 117 to 121 | 44 to 46 | 89 to 119 | 115 to 121 | 114 to 118 | 85 to 122 | -- | 85 to 127 | | Notched Izod Impact (ft·lb/in) | 0.00 to 18.0 | 1.45 to 15.0 | 3.27 to 30.0 | 0.618 to 16.5 | 0.937 to 18.1 | 0.0937 to 21.0 | 2.25 to 11.2 | 1.00 to 18.0 | 1.57 to 12.0 | | DTUL at 66 psi (0.45 MPa) (°F) | 269 to 290 | 254 to 280 | 215 to 253 | 205 to 268 | 238 to 278 | 172 to 257 | 298 to 300 | 207 to 229 | 329 | | DTUL at 264 psi (1.8 MPa) (°F) | 243 to 285 | 177 to 265 | 209 to 216 | 137 to 225 | 189 to 251 | 167 to 236 | 257 to 288 | 138 to 167 | 270 to 302 | | CLTE, Flow (in/in/°F) | 0.000029 to 0.000049 | 0.000035 to 0.000039 | 0.000052 | 1.7E-6 to 1.0 | 0.000024 to 0.000047 | 0.000032 to 0.000064 | 0.000033 to 0.86 | 0.000050 to 0.000089 | 0.000033 to 0.000051 |
SI
|
| Specific Gravity (g/cm³) | 1.16 to 1.22 | 1.14 to 1.22 | 1.15 | 1.18 to 1.24 | 1.19 to 1.22 | 1.19 to 1.20 | 1.20 | 1.21 to 1.22 | 1.20 | | Melt Mass Flow Rate (g/10 min) | 3.8 to 26 | 1.3 to 36 | 1.5 to 15 | 6.2 to 16 | 8.0 to 35 | 4.0 to 22 | 5.6 to 30 | 9.2 to 21 | 2.0 to 3.0 | | Flexural Modulus (MPa) | 1900 to 2660 | 1940 to 2770 | 1930 to 2490 | 1450 to 2280 | 1830 to 2440 | 1570 to 2330 | 2120 to 2300 | 28.7 to 1040 | 2030 to 2350 | | Tensile Strength (MPa) | 52.5 to 70.0 | 49.3 to 62.3 | 41.4 to 62.7 | 37.7 to 61.0 | 44.2 to 56.3 | 45.9 to 63.4 | 59.8 to 70.0 | 11.3 to 41.7 | 64.7 to 78.0 | | Tensile Elongation (%) | 0.0 to 120 | 1.7 to 94 | 3.7 to 11 | 1.5 to 150 | 3.0 to 54 | 2.0 to 150 | 6.0 to 86 | 120 to 180 | 6.0 to 120 | | Rockwell Hardness | 70 to 121 | 117 to 121 | 44 to 46 | 89 to 119 | 115 to 121 | 114 to 118 | 85 to 122 | -- | 85 to 127 | | Notched Izod Impact (J/m) | 0.00 to 961 | 77.3 to 801 | 175 to 1600 | 33.0 to 880 | 50.0 to 966 | 5.00 to 1120 | 120 to 600 | 53.4 to 961 | 84.0 to 641 | | DTUL at 66 psi (0.45 MPa) (°C) | 132 to 143 | 123 to 138 | 102 to 123 | 96.3 to 131 | 115 to 137 | 77.9 to 125 | 148 to 149 | 97.3 to 109 | 165 | | DTUL at 264 psi (1.8 MPa) (°C) | 117 to 140 | 80.6 to 129 | 98.2 to 102 | 58.1 to 107 | 87.0 to 122 | 74.8 to 113 | 125 to 142 | 59.0 to 75.3 | 132 to 150 | | CLTE, Flow (cm/cm/°C) | 0.000052 to 0.000087 | 0.000063 to 0.000070 | 0.000094 | 3.0E-6 to 1.9 | 0.000043 to 0.000084 | 0.000058 to 0.00011 | 0.000060 to 1.5 | 0.000090 to 0.00016 | 0.000060 to 0.000092 |
|
|