| Polycaprolactone (PCL) Typical Properties |
|
|
|
-
-
-
|
English
|
| Specific Gravity | 1.11 to 1.30 | | Melt Mass Flow Rate (g/10 min) | 3.0 to 40 | | Flexural Modulus (psi) | 74400 to 325000 | | Tensile Strength (psi) | 750 to 6000 | | Tensile Elongation (%) | 650 to 800 | | Rockwell Hardness | 105 | | Notched Izod Impact (ft·lb/in) | 2.25 to 10.0 | | DTUL at 66 psi (0.45 MPa) (°F) | -- | | DTUL at 264 psi (1.8 MPa) (°F) | 150 | | CLTE, Flow (in/in/°F) | 0.000025 to 0.000092 |
SI
|
| Specific Gravity (g/cm³) | 1.11 to 1.30 | | Melt Mass Flow Rate (g/10 min) | 3.0 to 40 | | Flexural Modulus (MPa) | 513 to 2240 | | Tensile Strength (MPa) | 5.17 to 41.4 | | Tensile Elongation (%) | 650 to 800 | | Rockwell Hardness | 105 | | Notched Izod Impact (J/m) | 120 to 534 | | DTUL at 66 psi (0.45 MPa) (°C) | -- | | DTUL at 264 psi (1.8 MPa) (°C) | 65.6 | | CLTE, Flow (cm/cm/°C) | 0.000045 to 0.00017 |
|
|